Method of removing binder material from a shaped ceramic preform by extracting with supercritical fluid
AssigneeSumitomo Heavy Industries, Ltd.
InventorsNobuaki Nakajima, Seiji Yasuhara, Mamoru Ishihara
Life of this patent
Estimating the term…
Abstract
The invention relates to a method of removing binder materials from a shaped preform (green body) in the preparation procedure for the manufacture of ceramics from particulate materials. The new method comprises exposing the green body to a supercritical fluid to dissolve the binder materials in the supercritical fluid without deforming the shape of the article. In the method, the binder materials can be removed without swelling of the article because the green body is not exposed to a rapid temperature increase and the binder does not volatilize in the body. In addition, the binder material can be removed in a drastically shorter period of time from the entire body.
Claims16
A process for removing binder material(s) from a preform in a prefiring preparation for the production of ceramics in a given shape, which comprises the steps of:
- (a) exposing a preform comprising refractory particulate material(s) and binder material(s) to a supercritical fluid which is gaseous under ambient pressure and ambient temperature thereby dissolving the binder material(s) in the fluid;
- (b) discharging the fluid from a vessel under supercritical condition;
- and
- (c) isolating the binder materials from the fluid by decreasing the density of the fluid thereby to recover the binder materials and fluid for further use thereof.
A method for the production of ceramics in a given shape, which comprises the steps of:
- (a) forming a preform in a given shape from refractory particulate materials and binder material(s) in controlled amount;
- (b) removing said binder material(s) from the preform by exposing the preform comprising the refractory particulate material and binder material(s) in a given shape, to a supercritical fluid, the substance of which is gaseous under the ambient pressure and the ambient temperature thereby to dissolve binder materials in the fluid;
- (c) discharging the fluid from a vessel under supercritical conditions;
- (d) isolating the binder materials from the fluid by controlling the pressure or the temperature of the fluid thereby to recover the binder materials and fluid for further use thereof;
- and then,
- (e) sintering the resulting preform into ceramics in the given shape.
A method of producing an article from a fired particulate configuration whereby binder material is removed from the particulate configuration prior to firing without deformation of the configuration prior to the firing thereof, comprising the steps of:
- (a) mixing together predetermined amounts of sinterable particulate material and binder whereby said binder covers substantially all of the surface of the particles of said particulate material;
- (b) forming said mixture into a desired configuration;
- (c) exposing said configuration to a supercritical fluid, the substance of which is gaseous under the ambient pressure and the ambient temperature whereby to dissolve and binder materials into the fluid;
- (d) isolating the binder materials from the fluid by controlling the pressure or the temperature of the fluid thereby to recover the binder materials and fluid for further use thereof, and then,
- (e) sintering said formed configuration.
Dependencies are inferred from the claim text.