Rapidly solidified aluminum based alloys containing silicon for elevated temperature applications
AssigneeAllied Corporation
InventorDavid J. Skinner
Life of this patent
Estimating the term…
Abstract
A rapidly solidified aluminum-base alloy consists essentially of the formula Al.sub.bal Fe.sub.a Si.sub.b X.sub.c, wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 1.5 to 7.5 atom percent, "b" ranges from 0.75 to 9.0 atom percent, "c" ranges from 0.25 to 4.5 atom percent and the balance is aluminum plus incidental impurities, with the proviso that the ratio [Fe+X]:Si ranges from about 2.01:1 to 1.0:1. The alloy exhibits high strength, ductility and fracture toughness and is especially suited for use in high temperature structural applications such as gas turbine engines, missiles, airframes and landing wheels.
Claims12
A rapidly solidified aluminum-base alloy consisting essentially of the formula Al.sub.bal Fe.sub.a Si.sub.b X.sub.c, wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 1.5 to 7.5 at %, "b" ranges from 0.75 to 9.0 at %, "c" ranges from 0.25 to 4.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio [Fe+X]:Si ranges from about 2.01:1 to 1.0:1.
A method for forming a consolidated metal alloy article;
- wherein particles composed of an aluminum-base alloy consisting essentially of the formula Al.sub.bal Fe.sub.a Si.sub.b X.sub.c, wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 1.5 to 7.5 at %, "b" ranges from 0.75 to 9.0 at %, "c" ranges from 0.25 to 4.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio [Fe+X]:Si ranges from about 2.01:1 to 1.0:1 are heated in a vacuum to a temperature ranging from about 300.degree. to 500.degree. C. and compacted.
A method for forming a consolidated metal alloy article wherein:
- (a) particles composed of an aluminum-base alloy consisting essentially of the formula Al.sub.bal Fe.sub.a Si.sub.b X.sub.c, wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 1.5 to 7.5 at %, "b" ranges from 0.75 to 9.0 at %, "c" ranges from 0.25 to 4.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio [Fe+X]:Si ranges from about 2.01:1 to 1.0:1 are placed in a container, heated to a temperature ranging from about 300.degree. to 500.degree. C., evacuated and sealed under vacuum, and
- (b) said container and contents are heated to a temperature ranging from 300.degree. to 500.degree. C. and compacted.
A consolidated metal article compacted from particles of an aluminum base alloys consisting essentially of the formula Al.sub.bal Fe.sub.a Si.sub.b X.sub.c, wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 1.5 to 7.5 at %, "b" ranges from 0.75 to 9.0 at %, "c" ranges from 0.25 to 4.5 at % and the balance is aluminum plus incidental impurities, the ratio [Fe+X]:Si ranging from about 2.01:1 to 1.0:1, said consolidated article being composed of an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates measuring less than about 100 nm. in any dimension thereof.