Flame retardant adhesive compositions
AssigneeEastman Kodak Company
InventorsRichard L. McConnell, Donald C. Davis, Frederick D. Petke, Max F. Meyer, Jr.
Life of this patent
Estimating the term…
Abstract
Disclosed are hot-melt adhesive compositions comprising discrete particles of polyester adhesives, discrete particles of polyester containing a halogenated organic compound and discrete particles containing an antimony compound. Also disclosed is a method of incorporating both a halogenated organic compound and an antimony compound into a polyester adhesive composition.
Claims11
A polyester adhesive composition in particulate form comprising a generally uniform mixture of discrete particles of
- (a) a thermoplastic polyester adhesive having a melting temperature of about 80.degree.-180.degree. C. and a heat of fusion of less than 10 calories/gram,
- (b) a polyester compatible with (a) having dispersed therein a chlorinated or brominated flame retardant compound, and
- (c) a polyester compatible with (a) and (b) having dispersed therein an antimony flame retardant compound having the ability to enhance the flame retarding characteristics of said chlorinated or brominated compound, the chlorinated or brominated compound of (b) and the antimony compound of (c) being present in said polyester adhesive composition in amounts of about 1-25% each based on the total composition weight.
The method of preparing a polyester adhesive composition having reduced flammability characteristics comprising the steps of
- (a) preparing a first concentrate in particulate form of a polyester having a chlorinated or brominated flame retardant compound dispersed therein,
- (b) preparing a second concentrate in particulate form of a polyester having dispersed therein an antimony compound having the ability to enhance the flame retarding characteristics of said chlorinated or brominated compound,
- (c) mixing said first and second concentrates with a particulate thermoplastic polyester adhesive having a melting temperature of about 80.degree.-180.degree. C. and a heat of fusion of less than 10 calories per gram, the particles being of a size compatible with the particles of said first and second concentrates, and the proportions of said first and second concentrates being such that the adhesive composition has a concentration of chlorinated or brominated compound, and antimony compositions of about 1-25% each, based on the total weight of the adhesive composition, and not exceeding a total of about 30 wt % of halogenated compound and antimony compound.