Amorphous silicon semiconductor film and production process thereof
AssigneeToa Nenryo Kogyo Kabushiki Kaisha
InventorsMitsuo Matsumura, Toshihiko Yoshida
Life of this patent
Estimating the term…
Abstract
This invention discloses an amorphous silicon semiconductor film comprising at least hydrogen, nitrogen, and oxygen as impurities and the method of producing it. The film is characterized in that the total quantity of nitrogen and oxygen in said film is at least 1 atom %. Since the film has a small light absorption coefficient and its optical refractive index is controllable, an excellent window material for solar cell can be provided. As adherence of the film with a metal electrode as well as with a transparent electrode is sufficient, good reproducibility in making solar cells using the film of this invention as window material was realized.
Claims5
A solar cell including an amorphous silicon semiconductor film as a window of said solar cell, said film having a refractive index of 2.8 to 3.4, the total quantity of nitrogen and oxygen within said film being from 1 to below 4 atom %.
A process of producing an amorphous silicon semiconductor thin film as a window layer for a solar cell, said film containing at least hydrogen, nitrogen, and oxygen as impurities, the total amount of nitrogen and oxygen being in the range from 1 atom % to below 4 atom % and having a refractive index of 2.8 to 3.4, characterized by using as a starting material one or more gaseous substance selected from the group consisting of silane, polysilane or their derivatives, and further characterized by using at least one gas selected from the group consisting of NO, NO.sub.2, and (N.sub.2 +O.sub.2) and decomposing these starting materials by plasma glow discharge under the following conditions;
- Power density:
- 0.01-2 W/cm.sup.2,
- Gas flow rate:
- 1-100 SCCM
- Substrate temperature:
- 100.degree.-400.degree. C.
- Pressure during discharge:
- 0.05-2 Torr,
- (nitrogen and oxygen sources/Si source) ratio:
- <0.1 (by volume),
- to form said silicon thin film as a window layer on a substrate.