Methods for weld repairing hollow, air cooled turbine blades and vanes
AssigneeUnited Technologies Corporation
InventorsMichael F. Foster, Thomas A. Ferguson
Life of this patent
Estimating the term…
Abstract
A mask particularly useful in the weld repair of air cooled gas turbine blades and vanes contains a mixture of ceramic particles in a liquid carrier. The mask is applied onto the surface of the blade or vane, and into the cooling holes. Following a sintering treatment, an inert, thermally stable, electrically nonconductive ceramic mask is produced, which is easily removed after welding.
Claims9
A method for keeping a portion of a metal article substantially free from molten weld filler metal during welding, comprising the steps of applying a compound containing ceramic particles in a liquid carrier to the portion of the article to be kept free of the filler metal, and heating the article to remove the liquid carrier from the mixture and to sinter the ceramic particles to each other to form a thermally stable ceramic mask which is nonreactive with the metal article and with the molten filler metal, and readily removable from the welded article.
A method for the arc weld repair of a hollow, air cooled metal article having a plurality of small diameter cooling holes, the method comprising the steps of filling the holes with a compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency;
- heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, electrically nonconductive, nonreactive ceramic mask which fills the cooling holes after sintering;
- welding the metal article, wherein the ceramic mask prevents molten weld metal from entering and solidifying in the holes;
- and removing the ceramic mask from the holes.
A method for arc weld repairing an air cooled, hollow turbine blade having a tip portion, a squealer pocket, and an airfoil portion, wherein the blade has a plurality of small diameter cooling holes in the tip portion, the squealer pocket, and the airfoil portion, and wherein some of the holes are shaped holes, the method comprising the steps of filling the squealer pocket and the cooling holes and coating the airfoil portion with compound containing ceramic particles in a liquid carrier, the mixture having a paste-like consistency;
- heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable, nonreactive, electrically nonconductive ceramic mask which fills the squealer and the cooling holes after sintering;
- arc weld repairing the tip portion of the blade by depositing a layer of filler metal on the blade tip surface, wherein the ceramic mask in the squealer pocket prevents the weld metal from solidifying in the squealer, the ceramic mask in the cooling holes prevents the weld metal from solidifying in the holes and the ceramic mask on the airfoil portion prevents the weld metal from solidifying on the airfoil;
- and removing the ceramic mask from the blade.
A method for the arc weld repair of a defect in a metal article having an internal cavity, comprising the steps of inserting a paste-like compound containing ceramic particles in a liquid carrier in the cavity;
- heating the article to remove the liquid carrier from the compound and to sinter the ceramic particles to each other to form a thermally stable nonreactive ceramic mask in the internal cavity;
- machining away the defect without removing a substantial amount of the mask;
- weld repairing the defect;
- and removing the ceramic mask.
A mixture sinterable to form a mask used during the weld repair of a metal article, consisting essentially of a mixture of silica, zircon, and alumina fiber, and an amount of colloidal silica to form a paste-like consistency.
Dependencies are inferred from the claim text.