Gas shielded, flux cored, welding electrode
AssigneeThe Lincoln Electric Company
InventorsRobert P. Munz, John R. Gonzalez, Ronald J. Gordish
Life of this patent
Estimating the term…
Abstract
A flux cored welding electrode for use in electric arc welding with a shielded gas, which electrode includes a tube of low carbon steel having on the inside thereof a titanium dioxide based flux with fluxing ingredients including aluminum oxide in the amount of 0.1 to 0.5% of the total weight of the electrode. The improvement of the invention wherein the titanium dioxide based flux with aluminum oxide free of magnesium or compounds of magnesium.
Claims8
A flux cored welding electrode for use in electric arc welding with a shielding gas, comprised of a tube of low carbon steel, having on the inside thereof titanium dioxide based flux with fluxing ingredients including aluminum oxide in amounts of from 0.1 to 5.0 percent of the total weight of the electrode, the titanium dioxide based flux with aluminum oxide being free of magnesium or compounds of magnesium.
A flux cored electrode for gas shielded electric arc welding comprising in combination:
- a tube of low carbon steel, having on the inside thereof, a titanium dixode based flux fill of from 10 to 20% of the total weight of the electrode, said flux fill containing aluminum oxide in amounts of from 0.54% to 27.0% and no magnesium.
A flux cored tubular electrode for electric arc welding using a shielding gas, comprised of a low carbon steel tube containing on the inside a flux formulation comprising titanium dioxide, other metallic oxides selected from the class consisting of silicon potassium and sodium, steel alloying ingredients selected from the class consisting of silicon, manganese, nickel, chromium, vanadium and boron, fluoride compounds selected from the class consisting of the fluorides of calcium, potassium, sodium, barium;
- the improvement which comprises aluminum oxide of from 0.1 to 5.0 percent of the total electrode weight, there being no magnesium in said flux formulation.
A flux cored electrode for electric arc welding, using a shielding gas, comprised of a low carbon steel tube having a flux on the inside thereof, said flux comprising titanium dioxide and silicon, potassium and sodium oxides in approximate total amounts of such metal oxides being from 25% to 60% of said flux, steel alloying ingredients in said flux selected from the class consisting of silicon, manganese, nickel, chromium and boron in approximate total amounts of from 13% to 30% of said flux, calcium fluoride in approximate amounts of 0.0% to 10% of said flux, the improvement which comprises aluminum oxide of from 0.1 to 5.0 percent of the total electrode weight, said flux being magnesium free.
A flux cored welding electrode for gas shielded electric arc welding comprising in combination a tube of low carbon steel having on the inside thereof the following flux ingredients in the approximate amounts stated:
- Sodium Oxide:
- 0.50
- Aluminum Oxide:
- 1.20
- Silicon Dioxide:
- 1.57
- Titanium Dioxide:
- 4.44
- Calcium Fluoride:
- 0.19
- Silicon:
- 0.98
- Manganese:
- 2.69
- Iron:
- 6.56
- all stated as a percent of the total electrode weight.
A flux cored welding electrode for gas shielded electric arc welding comprising in combination a tube of low carbon steel having on the inside thereof the following flux ingredients in the approximate amounts stated:
- Sodium Oxide:
- 0.27
- Potassium Oxide:
- 0.11
- Aluminum Oxide:
- 2.47
- Silicon Dioxide:
- 1.05
- Titanium Dioxide:
- 5.8
- Zirconium Dioxide:
- 0.11
- Calcium Fluoride:
- 0.15
- Boron:
- 0.002
- Silicon:
- 0.84
- Manganese:
- 2.59
- Iron:
- 1.17
- all stated as a percent of the total electrode weight.