Lightly crosslinked linear olefinic polymer foams and process for making
AssigneeThe Dow Chemical Company
InventorChung P. Park
Life of this patent
Estimating the term…
Abstract
A substantially closed-celled linear polyolefin foam is made by melt processing under pressure a linear polyolefin together with a volatile blowing agent and a crosslinking agent and then expanding the polymer. Suitable crosslinking agents, including azido and vinyl functional silanes, organic peroxides, multifunctional vinyl monomers, and oxygen, increase the melt tension and melt viscosity of the polymer by lightly crosslinking the polymer with itself to enable the production of foams having improved properties in comparison with branched polyolefin foams.
Claims12
A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure, comprising the steps of:
- (a) melt processing under pressure a linear olefin polymer or blend of linear olefin polymers,
- (b) mixing a volatile blowing agent and a sufficient amount of one crosslinking agent selected from the group consisting of azido functional silanes. multifunctional vinyl monomers, and oxygen, together with said linear olefin polymer or blend of linear olefin polymers to form a flowable admixture, and,
- (c) extruding said admixture through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend of linear olefin polymers to a closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.
A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure, comprising the steps of:
- (a) melt process under pressure a linear olefin polymer or blend of linear olefin polymers together with a volatile blowing agent to form a flowable admixture,
- (b) introducing an amount of crosslinking agent sufficient to initiate crosslinking of said linear olefin polymer or blend and increase the pressure of said admixture to at least 400 psig, said crosslinking agent consisting of one of azido functional silanes, multifunctional vinyl monomers, or oxygen, and
- (c) extruding said admixture through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.
A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure comprising the steps of:
- (a) melt processing under pressure a linear olefin polymer or blend of linear olefin polymers,
- (b) mixing a volatile blowing agent and a sufficient amount of a crosslinking agent selected from the group consisting of azido functional silanes, multifunctional vinyl monomers, oxygen, and mixtures thereof, together with said linear olefin polymer or blend of linear olefin polymers to form a flowable admixture, and,
- (c) extruding said admixtures through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend of linear olefin polymers to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.
Dependencies are inferred from the claim text.