AssigneeMartin Marietta Corporation
InventorsJohn M. Brupbacher, Leontios Christodoulou, Dennis C. Nagle
Life of this patent
Estimating the term…
Abstract
A method is taught for the in-situ precipitation of ceramic materials in a metal matrix. By means of the solvent assisted reaction, metal-ceramic composites having highly superior properties may be obtained. The invention involves the reaction of the ceramic forming constituents in a metal solvent medium to provide very finely-dispersed ceramic particles in the metal matrix. Exemplary materials include titanium diboride in an aluminum matrix.
Claims43
A method for the production of metal-ceramic composite materials containing a ceramic phase, said method comprising precipitating at least one ceramic material in a metal matrix by contacting reactive ceramic forming constituents, in the presence of a non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase, at a temperature at which sufficient diffusion of said constituents into said solvent matrix metal occurs to cause reaction of said reactive ceramic forming constituents raising the temperature above the melting temperature of the matrix metal to precipitate said ceramic phase in said solvent matrix metal.
A method for precipitation of a ceramic phase in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal to initiate an exothermic reaction;
- (c) permitting said exothermic reaction to further heat the mixture and to form a uniform distribution of ceramic particles;
- and
- (d) recovering a product.
A method for the uniform dispersion of ceramic dispersoids in a metal matrix, said method comprising forming a reaction mixture of reactive ceramic forming constituents in the presence of at least two solvent metals in which ceramic forming constituents are more soluble than said ceramic dispersoids, raising the temperature of said reaction mixture to a temperature at which sufficient diffusion of the ceramic forming constituents into the lowest melting solvent metal occurs to initiate reaction of said constituents, whereby the exothermic heat of reaction of said constituents causes the temperature of the reaction mixture to exceed the melting point of the matrix of the higher melting metal permitting uniform dispersion of said ceramic dispersoid in a matrix of higher melting metal or an alloy thereof.
A method for the in-situ precipitation of at least one intermetallic material in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic forming constituents and a non-reactive solvent matrix metal in which said intermetallic forming constituents are more soluble than said intermetallic material;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of said mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic forming constituents;
- and
- (d) recovering a product.
A method for the in-situ precipitation of dispersoid particles of at least one intermetallic material and at least one ceramic material in a metal matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic and ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said intermetallic and ceramic forming constituents are more soluble than said intermetallic material and said at least one ceramic material, respectively;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of the mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic and ceramic forming constituents;
- and
- (d) recovering a product.
A method for the production of metal-ceramic composite materials containing a ceramic phase, said method comprising precipitating at least one ceramic material in a metal matrix by contacting reactive ceramic forming constituents, in the presence of a non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase, at a temperature at which sufficient diffusion of said constituents into said solvent matrix metal occurs to cause reaction of said reactive ceramic forming constituents raising the temperature above the melting temperature of the matrix metal to precipitate a substantially uniform distribution of said ceramic phase in said solvent matrix metal.
A method for the in-situ precipitation of a substantially uniform distibution of at least one intermetallic material in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic forming constituents and a non-reactive solvent matrix metal in which said intermetallic forming constituents are more soluble than said intermetallic material;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of said mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic forming constituents;
- and
- (d) recovering a product.
A method for the in-situ precipitation of a substantially uniform distribution of dispersoid particles of at least one intermetallic material and at least one ceramic material in a metal matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic and ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said intermetallic and ceramic forming constituents are more soluble than said intermetallic material and said at least one ceramic material, respectively;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of the mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic and ceramic forming constituents;
- and
- (d) recovering a product.
A method for the production of metal-ceramic composite materials containing a ceramic phase, said method comprising precipitating at least one ceramic material in a metal matrix by contacting reactive ceramic forming constituents, in the presence of a non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase, at a temperature at which sufficient diffusion of more than a localized portion of said constituents into said solvent matrix metal occurs to cause reaction of said reactive ceramic forming constituents raising the temperature of said reactive ceramic forming constituents above the melting temperature of the matrix metal to precipitate said ceramic phase in said solvent matrix metal.
A method for precipitation of a ceramic phase in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase;
- (b) heating more than a localized portion of the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal to initiate an exothermic reaction;
- (c) permitting said exothermic reaction to further heat the mixture and to form ceramic particles;
- and
- (d) recovering a product.
A method for the substantially uniform dispersion of ceramic dispersoids in a metal matrix, said method comprising forming a reaction mixture of reactive ceramic forming constituents in the presence of at least two solvent metals in which ceramic forming constituents are more soluble than said ceramic dispersoids, raising the temperature of more than a localized portion of said reaction mixture to a temperature at which sufficient diffusion of the ceramic forming constituents into the lowest melting solvent metal occurs to initiate reaction of said constituents, whereby the exothermic heat of reaction of said constituents causes the temperature of the reaction mixture to exceed the melting point of the matrix of the higher melting metal permitting substantially uniform dispersion of said ceramic dispersoid in a matrix of higher melting metal or an alloy thereof.
A method for the in-situ precipitation of at least one intermetallic material in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic forming constituents and a non-reactive solvent matrix metal in which said intermetallic forming constituents are more soluble than said intermetallic material;
- (b) heating more than a localized portion of the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of said mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic forming constituents;
- and
- (d) recovering a product.
A method for the in-situ precipitation of dispersoid particles of at least one intermetallic material and at least one ceramic material in a metal matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive intermetallic and ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said intermetallic and ceramic forming constituents are more soluble than said intermetallic material and said at least one ceramic material, respectively;
- (b) heating more than a localized portion of the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal;
- (c) permitting the resultant exothermic reaction to raise the temperature of the mixture to a temperature exceeding the melting point of the matrix metal and to consume intermetallic and ceramic forming constituents;
- and
- (d) recovering a product.
A method for precipitation of a ceramic phase in a metallic matrix, said method comprising the steps of:
- (a) preparing a mixture of reactive ceramic forming constituents and a substantially non-reactive solvent matrix metal in which said ceramic forming constituents are more soluble than said ceramic phase;
- (b) heating the mixture to a reaction initiation temperature approximating the melting point of the solvent matrix metal to initiate an exothermic reaction;
- (c) permitting said exothermic reaction to further heat the mixture and to form ceramic particles;
- and
- (d) recovering a product.