Silicon-containing polyimides as oxygen etch stop and dual dielectric coatings

Abstract

The use of silicon-containing polyimide as an oxygen etch barrier in a metal lift-off process and as an oxygen etch stop in the fabrication of multi-layer metal structures is described. In practice, a lift-off layer is applied on a substrate, followed by a layer of silicon-containing polyimide and a layer of photoresist. The photoresist is lithographically patterned, and the developed image is transferred into the silicon-containing polyimide layer with a reactive ion etch using a CF.sub.4 /O.sub.2 gas mixture. The pattern is transferred to the lift-off layer in a reactive ion etch process using oxygen. Subsequent blanket metal evaporation followed by removal of the lift-off stencil results in the desired metal pattern on the substrate. In an alternate embodiment, the silicon-containing polyimide can be doped with a photoactive compound reducing the need for a separate photoresist imaging layer on the top.