Methods for reducing the water content of optical waveguide fibers

A method for reducing the water content of an optical waveguide fiber formed by drawing a glass blank, said glass blank having (1) an aperture therethrough, (2) being formed at an elevated temperature, and (3) including regions whose thermal coefficients of expansion differ by at least about 7.times.10.sup.-7 cm/cm.degree.C. such that the blank's probability of fracture if cooled to room temperature is at least about 75 percent, the method comprising the steps of:

• (a) cooling the blank from the elevated temperature to a temperature within a preselected temperature range, the blank's probability of fracture within said range being below about 50 percent, the low end of said range being above room temperature and the high end of said range being below about 550.degree. C., said range being selected to minimize the diffusion of water from the surface of the aperture into the body of the blank;
• (b) maintaining the temperature of the blank within the preselected temperature range for a period of time of up to about 48 hours until drawing is to be performed;
• and
• (c) drawing the blank at an elevated temperature while applying a vacuum to the aperture, the elevated temperature and the vacuum removing sufficient water from the blank prior to aperture closure so as to produce a finished fiber having a water level of less than 100 parts per billion.