Process for the continuous preparation of homogeneous solutions of high molecular polymers
AssigneeStamicarbon B.V.
InventorsPieter J. Lemstra, Henricus E. H. Meijer, Lambert H. T. van Unen
Life of this patent
Estimating the term…
Abstract
A continuous process is described wherein suspensions of high molecular weight polymers are readily transformed into solutions thereof for extrusion, to make gel filaments, tapes, tubes and films, by use of an extruder having alternate mixing and transporting sections and operating at mechanical shear rates of from 30 to 2,000 sec..sup.-1, and with relatively short residence times therein.
Claims14
Process for the continuous preparation of homogeneous solutions up to 50 wt.% of high-molecular weight polymers which comprises forming a suspension of a finely divided high-molecular weight polymer in a suitable solvent or mixture of solvents, which solvent(s) is (are) liquid at room temperature, and processing said suspension through a screw extruder operated at a rotational speed of from about 30 to about 300 revolutions/minute, and equipped with alternate mixing and conveying sections, during such a required residence time (t) in the extruder that (t) expressed in minutes is at most 0.3 D, wherein D denotes the diameter of said extruder expressed in millimeters, at a temperature above the dissolution temperature of said polymer in said solvent(s) at the prevailing operating pressure, and employing a mixing and kneading treatment therein at a mechanical shear rate between about 30 and 2000 sec..sup.-1 whereby a homogeneous solution of said polymer is formed containing at least 50 wt.% of solvent.
A process for the continuous forming of highly stretchable gel filaments, tapes, tubes and films from suspensions of high molecular weight polymers which comprises processing a 1-50 wt. % suspension of a finely divided polymer in a suitable solvent or mixture of solvents which solvent(s) is (are) liquid at room temperature, through a screw extruder operated at a rotational speed of from 30 to about 300 r.p.m. and equipped with alternate mixing and conveying sections, during such a required residence time (t) in said extruder that (t) expressed in minutes is at most 0.3 D, wherein D denotes the diameter of said extruder expressed in millimeters, at a temperature above the dissolution point of said polymer in said solvent(s) and below the boiling point of the solvent(s) at the prevailing operating pressure, while employing a mixing and kneading treatment therein with a mechanical shear rate between about 30 and 2,000 sec..sup.-1, whereby a homogeneous solution containing at least 50 wt. % solvent is formed, and thereafter passing the thus-formed homogeneous solution out of the extruder thus obtained to below the gel-point to obtain a homogeneous gel filament, tape, film or tube, according to the configuration of the said orifice.
Process for the continuous preparation of homogeneous solutions up to 50 wt.% of high-molecular weight polymers which comprises forming a suspension of a finely divided high-molecular weight polymer in a suitable solvent or mixture of solvents, which solvent(s) is (are) liquid at room temperature, and processing said suspension through a co-rotation twin-screw extruder operated at a rotational speed of from about 30 to about 300 revolutions/minute, and equipped with alternate mixing and conveying sections, during such a required residence time (t) in the extruder that (t) expressed in minutes is at most 0.3 D, wherein D denotes the diameter of said extruder expressed in millimeters, at a temperature above the dissolution temperature of said polymer in said solvent(s) at the prevailing operating pressure, and employing a mixing and kneading treatment therein at a mechanical shear rate between about 30 and 2000 sec..sup.-1 whereby a homogeneous solution of said polymer is formed containing at least 50 wt. % of solvent.