Formation of intermetallic and intermetallic-type precursor alloys for subsequent mechanical alloying applications
AssigneeInco Alloys International, Inc.
InventorsPaul S. Gilman, Arun D. Jatkar, Stephen Donachie, Winfred L. Woodard, III, Walter E. Mattson
Life of this patent
Estimating the term…
Abstract
A method for forming intermetallic and intermetallic-type precursor alloys for subsequent mechanical alloying applications. Elemental powders are blended in proportions approximately equal to their respective intermetallic compounds. Heating of the blend results in the formation of intermetallic compounds whereas lack of heating results in intermetallic-type powder without the intermetallic structure. The resultant powder is then blended to form a final alloy. Examples involving aluminum-titanium alloys are discussed.
Claims9
A method for making homogeneous intermetallic dispersion strengthened powder compositions, the method comprising:
- (a) blending elemental powders comprising the intermetallic composition and a process control agent into a blend, the elemental powders including a principal element and at least one secondary element, the secondary element having a different hardness than the principal element,
- (b) mechanically alloying the blend, and
- (c) heating the blend below the solidus temperature of all of the elements to form the intermetallic composition.
A method for forming homogeneous intermetallic dispersion strengthened Al.sub.3 Ti powder, the method comprising:
- (a) blending about 62.8% aluminum powder and about 37.2% titanium powder,
- (b) mechanically alloying the aluminum-titanium powder blend in a non-oxidizing environment, and
- (c) heating the blend to a temperature below the solidus temperature of aluminum so as to form an aluminum-titanium intermetallic composite power.
A method for forming a homogeneous intermetallic dispersion strengthened aluminum-base alloy powder, the method comprising:
- (a) blending aluminum powder and at least one secondary element powder in the same proportions as a corresponding intermetallic composition, to form a blend,
- (b) mechanically alloying the blend, and
- (c) heating the composition to a temperature below the solidus temperature of each of the elements so as to form the intermetallic composition.
Dependencies are inferred from the claim text.