Method for rapidly removing binder from a green body
AssigneeFine Particle Technology Corp.
InventorRaymond E. Wiech, Jr.
Life of this patent
Estimating the term…
Abstract
The disclosure relates to a method of rapidly removing binder from a "green" body composed of metal or cermet fine particles and a carbon-containing binder wherein the debinderizing step is performed in a water saturated atmosphere to provide chemical reaction with elemental carbon, the reaction products being removed from the system.
Claims17
A method of producing an article from a fired particulate configuration whereby binder material is removed from the particulate configuration prior to firing without swelling the particulate configuration and consequent imparting of sheer or tensile force to the particulate configuration prior to the firing thereof, wherein said configuration is formed by mixing together predetermined amounts of sinterable particulate material and binder whereby the binder covers substantially all of the surface of the particles of said particulate material and forming said mixture into a desired configuration, comprising the steps of:
- (a) heating said configuration to a temperature above the flow point of at least a portion of said binder,
- (b) substantially saturating the atmosphere contacting the exposed surfaces of said configuration with water vapor after the temperature of the surface of said configuration is above 100.degree. C.,
- (c) moving said water saturated atmosphere over and in contact with said configuration,
- (d) elevating the temperature of said configuration with a predetermined temperature-time profile to a level below the sintering temperature of said particulate material to remove remaining binder from said configuration,
- (e) providing an atmosphere contacting said configuration suitable to the sintering requirements of said configuration;
- and
- (f) raising the temperature of said configuration according to a predetermined temperature-time profile to sinter said stripped and formed configuration.
A method of producing an article from a fired particulate configuration whereby binder material is removed from the particulate configuration prior to firing without swelling the particulate configuration and consequent imparting of sheer or tensile force to the particulate configuration prior to the firing thereof, wherein said configuration is formed by mixing together predetermined amouts of sinterable particulate material and binder whereby the binder covers substantially all of the surface of the particles of said particulate material and forming said mixture into a desired configuration, comprising the steps of:
- (a) providing an enclosure having an air atmosphere,
- (b) placing said configuration in said enclosure,
- (c) heating said configuration to a temperature above the flow point of at least a portion of said binder,
- (d) substantially saturating said atmosphere with water vapor after said configuration has been heated to a temperature in excess of 100.degree. C.,
- (e) causing said atmosphere to flow over and contact the surface of said configuration,
- (f) elevating the temperature of said configuration with a predetermined temperature-time profile to a level below the sintering temperature of said particulate material to remove remaining binder from said configuration,
- (g) providing an atmosphere containing said configuration suitable to the sintering requirements of said configuration;
- and
- (h) raising the temperature of said configuration according to a predetermined temperature-time profile to sinter said configuration.
Dependencies are inferred from the claim text.