Method for applying material to a substrate
AssigneeC4 Carbides Limited
InventorPeter J. Nicolson
Life of this patent
Estimating the term…
Abstract
The invention relates to a process for brazing refractory particles, notably tungsten carbide grits, onto a substrate such as a tool blank to provide an armor coating or a cutting edge thereon, which process comprises applying to the substrate a brazing material, a particulate refractory material to be brazed onto the substrate and a binder composition; and connecting the substrate to a source of an electric current to cause the current to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse. The invention also provides apparatus for carrying out the invention.
Claims12
A process for brazing refractory particles onto a substrate, which process comprises applying to the substrate a brazing material, a particulate refractory material to be brazed onto the substrate and a binder composition;
- and connecting the substrate to a source of an electric current to cause the current to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse.
A process for brazing refractory particles onto a steel tool blank substrate so as to form a grit cutting edge thereon, which process comprises:
- (a) applying to the substrate a brazing material selected from a cobalt-based and a nickel-based alloy;
- a particulate refractory material selected from the carbides, nitrides, borides and silicides of nickel and tungsten and having a mass median particle size in the range 0.01 to 6 mms;
- a binder composition comprising an acrylic polymeric material;
- and optionally a flux material selected from fluoride based fluxes and borax/boric acid mixtures;
- said materials being used in proportions of from 5 to 10 parts of refractory material, 1 to 2 parts of brazing material, from 2 to 5 parts of binder composition and, optionally, from 1 to 2 parts of flux, all parts being by dry weight;
- (b) connecting the substrate to a source of an electric current to cause a current of from 50 to 250 amps at from 10 to 50 volts to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse in a protective atmosphere at part of which is provided by volatilisation and decomposition products from the binder composition;
- and
- (c) optionally re-heating the brazed substrate to cause thermal tempering thereof by passing a further electric current therethrough during cooling of the substrate following brazing.
A method for forming a brazed layer on a substrate wherein the flexible base material is removed from a substrate to expose the adherent interface binder composition, a brazeable coating material is applied to the exposed binder composition, and the coated substrate is subjected to heating to cause the coating to be fused to the substrate.
Dependencies are inferred from the claim text.