US 4,610,722 A · Process for metal recovery from steel plant dust

Abstract

A process is provided for hydrometallurgical processing of steel plant dusts containing cadmium, lead, zinc, and iron values, along with impurities such as chloride and fluoride salts of sodium, potassium, magnesium, etc. The first step in the process involves leaching the dust in a mixed sulfate-chloride medium that dissolves most of the zinc and cadmium. Any iron and aluminum dissolved in this step is precipitated by oxidation and neutralization. Zinc is recovered from the resulting solution by solvent extraction which provides a raffinate which is recycled to the leaching step with a bleed stream also provided for recovery of cadmium and removal of other impurities from the circuit. The lead sulfate residue from the leaching step is leached with caustic soda, and zinc dust is used to cement the lead out from the caustic solution, which then joins the main solution for zinc recovery. The residue from the lead leaching step is mixed with iron-aluminum oxide precipitate and agglomerated into pellets using cement. These pellets can be charged into steel furnaces for iron recovery or stored as a nontoxic waste.

Claims9

Dependent claims

A process for the hydrometallurgical treatment of steel plant dust containing iron, lead, zinc, and at least one of cadmium, aluminum, calcium, chlorides and fluorides of sodium, potassium and magnesium as impurities which comprises,

mixing a charge of said dust with an acid solution containing a mixture of hydrochloric acid and sulfuric acid, the amount of hydrochloric acid being at least stoichiometrically sufficient to react with and form a solution of at least one of zinc and cadmium, and maintain a pH in the range of about 1.5 to about 2.5,
the amount of sulfuric acid being at least stoichiometrically sufficient to react with lead and form a precipitate of lead sulfate,
leaching said dust with said solution at a temperature ranging from ambient up to the boiling point,
subjecting said solution of solid/liquid separation to remove the lead sulfate precipitate and provide a filtrate containing iron and zinc and at least one of aluminum and cadmium, oxidizing said filtrate and adding a neutralizing agent to raise the pH to a level selective to the precipitation of iron and aluminum present,
separating the precipitate from said filtrate containing zinc,
and selectively recovering zinc from said filtrate.

3 more elements

A process for the hydrometallurgical treatment of steel plant dust containing iron, lead, zinc, and at least one of cadmium, aluminum, calcium and chlorides and fluorides of sodium, potassium and magnesium as impurities which comprises,

providing steel plant dust containing
about 1% to 50% Fe
about 0.5% to 20% Pb
about 1% to 40% Zn
up to about 8% Al
up to about 2% Na
up to about 7% Cd
up to about 20% Cl
up to about 5% F
and the balance essentially oxygen associated with the above metals and insoluble oxides of CaO, SiO.sub.2, and MnO.sub.2,
mixing a charge of said dust with an acid leaching solution containing a mixture of hydrochloric acid and sulfuric acid,
the amount of hydrochloric acid being at least stoichiometrically sufficient to react with and form a solution of zinc and cadmium and maintain the pH in the range of about 1.5 to about 2.5,
the amount of sulfuric acid being at least stoichiometrically sufficient to react with lead and form a precipitate of lead sulfate,
leaching said dust with said solution at a temperature in the range of about 30.degree. C. to 90.degree. C.,
subjecting said solution to solid/liquid separation to remove the lead sulfate precipitate and provide a filtrate containing iron, aluminum, zinc and cadmium,
selectively dissolving the lead sulfate with a solution of caustic soda and recovering lead from said solution,
oxidizing said iron-containing filtrate and adding a neutralizing agent to raise the pH to a level selective to the precipitation of iron and aluminum as oxides,
separating the precipitated iron and aluminum oxides from said filtrate containing zinc and cadmium,
agglomerating said precipitate for use as recycled feed to steel furnaces,
selectively recovering zinc from said filtrate by solvent extraction using an organic solvent and providing a raffinate containing cadmium filtrate,
recovering cadmium from the raffinate, stripping said zinc from the organic solvent with an aqueous acid solution,
and recovering said zinc from said solution.

19 more elements

Dependencies are inferred from the claim text.

Process for metal recovery from steel plant dust