Process for making molding grade polyethylene terephthalate

AssigneeCelanese Corporation

InventorsGerald S. Kirshenbaum, Michael Goldin, W. Alan Case

Life of this patent

Estimating the term…

Loading patent…

Abstract

Polyethylene terephthalate (PET) produced by direct esterification of a mixture containing ethylene glycol and terephthalic acid in a mole ratio ranging from about 1.05 to about 1.35 dl/g, with at least about 325 parts of an antimony catalyst per million parts of polymer product, can be treated to reduce its acetaldehyde content and acetaldehyde generation rate and increase molecular weight to the levels required for the production of beverage bottles. After heat treatment to produce a crystallinity of at least about 10 percent, the PET can be used in molding after substantially conventional pre-drying and drying steps in air at the molding facility. The invention thus allows beverage bottle grade PET to be produced and prepared for molding without the conventional step of solid state polymerization or stabilization, saving energy, time, production costs and capital investment. Also disclosed is a process for molding a PET preform wherein the polymer prepared as described above is melted, formed into the desired preform shape, and solidified by cooling. This preform can then be reheated above its glass transition temperature and molded into the desired container shape.

Claims15

Dependent claims

An improved process for producing polyethylene terephthalate chip having levels of acetaldehyde content and acetaldehyde generation rate and intrinsic viscosity suitable for molding, said process comprising the steps of:

(a) introducing ethylene glycol and terephthalic acid to a reactor in a ratio of from about 1.05 to about 1.35 moles ethylene glycol per mole terephthalic acid and an antimony catalyst in a concentration in the range of from about 325 to about 600 parts antimony per million parts by weight of the product polymer, and heating the resulting mixture at a temperature in the range of about 240.degree. to about 260.degree. C. and a pressure in the range of from about 1 to about 5 atmospheres until said acid is at least about 95 percent esterified to form an esterified monomer mixture;
(b) melt polymerizing the antimony-containing esterified monomer mixture of step (a) in at least two stages at progressively higher temperatures in the range of from about 270.degree. to about 285.degree. C. and at a reduced pressure, until it attains an intrinsic viscosity of at least about 0.64 dl/g;
(c) extruding the melt of step (b) into a water bath for quenching, then pelletizing the quenched polymer so that the average individual volume chip is in the range of from about 2.3 to about 3.5 mm.sup.3 ;
and
(d) crystallizing the polymer pellets by heating in air or an inert atmosphere with agitation at a temperature in the range of about 110.degree. to about 160.degree. C. for a time effective to produce a degree of crystallinity in said polymer in the range of from about 10 percent to less than about 30 percent.

2 more elements

An improved process for producing polyethylene terephthalate suitable for molding, comprising the steps of:

(a) esterifying ethylene glycol by heating it in admixture with terephthalic acid and at least about 325 parts antimony catalyst per million parts of the polymer product in a ratio of about 1.05 to about 1.35 moles of said glycol per mole of said acid at a temperature in the range of from about 240.degree. to about 260.degree. C. and a pressure in the range of from about 1 to 5 atmospheres until said acid is at least about 95 percent esterified to form an esterified monomer mixture;
(b) melt polymerizing the antimony-containing monomer mixture of step (a) at a temperature in the range of from 270.degree. to 285.degree. C. and at a reduced pressure until it attains an intrinsic viscosity of at least about 0.64;
(c) extruding, quenching and pelletizing the melt product of (c) to form chip of an average volume in the range of from about 2.3 to about 3.5 mm.sup.3 ;
(d) crystallizing the polymer pellets of (c) by heating with agitation in air or an inert atmosphere at a temperature in the range of from about 110.degree. to about 160.degree. C. to produce a degree of crystallinity within the range of from about 10 to about 25 percent;
(e) transporting the pellets to a molding facility;
(f) pre-drying said crystallized polymer pellets in the molding facility at a temperature in the range of from about 145.degree. to about 165.degree. C. for a time in the range of about 1 to about 3 hours using air having a dew point below about -25.degree. C. flowing at a velocity of about 1 to 2 ft/sec.;
and
(g) thereafter drying said polymer pellets in a drier at a temperature in the range of about 180.degree. to about 225.degree. C. for a time in the range of about 2 to about 5 hours using air having a dew point below about -40.degree. C. flowing at a velocity of about 1 to 2 ft/sec.,
thereby producing a molding resin having a level of residual acetaldehyde less than about 3 parts per million, a generation rate of acetaldehyde less than about 4 parts per million per minute, and an intrinsic viscosity of at least about 0.68 deciliters per gram as calculated from measurements made on an 8 weight percent solution in o-chlorophenol at 25.degree. C.

6 more elements