Low volatile organic content cathodic electrodeposition baths
AssigneeInmont Corporation
InventorsTapan K. Debroy, Dave W. Braun, Ding-Yu Chung
Life of this patent
Estimating the term…
Abstract
A reactive diluent for use in an amine-containing epoxy resin composition. The reactive diluent comprises a soft, blocked isocyanate crosslinking agent. This reactive diluent is incorporated into the resin in addition to the primary crosslinking agent. The use of the reactive diluent eliminates or substantially reduces the need for volatile organic coalescent solvents and produces smooth, durable corrosion resistant coatings.
Claims6
In a cathodic electrodepositable resin composition comprising an epoxy resin/amine adduct, wherein the epoxy/amine-adduct is mixed with a primary crosslinking agent and salted to form a principle emulsion, the improvement comprising the inclusion of an additional crosslinking agent having Tg below ambient temperature as a reactive diluent in the principle emulsion, thereby producing a principle emulsion which, when incorporated into a coating bath, produces smooth electrodeposited films, thereby eliminating or substantially reducing the need for volatile organic coalescent solvents.
In a cathodic electrodeposition bath containing a mixture of a principle emulsion, wherein the principle emulsion comprises a salted epoxy resin/amine-adduct particularly adapted for use as a film forming composition in an electrodeposition process and a primary crosslinking agent, a pigment paste, and water, the improvement comprising the inclusion of an additional cross-linking agent having Tg below ambient temperature as a reactive diluent in the principle emulsion, thereby substantially reducing or eliminating the need for coalescent solvents in the coating bath and producing smooth electrodeposited films.
A method of electrocoating an object in a cathodic electrodeposition bath, comprising:
- forming an amine/epoxy resin adduct;
- mixing the adduct with a first crosslinking agent;
- mixing the adduct with a reactive diluent comprising a second, low Tg crosslinking agent;
- salting the adduct with an acid;
- thereby forming a principal emulsion;
- mixing the principal emulsion with a pigment paste and water to form a coating bath;
- connecting a conductive article to a DC electric circuit to act as a cathode and immersing the article in the bath;
- passing an electric current through the article, thereby depositing a film of resin and pigment paste on the article;
- removing the article from the bath and curing the deposited coating,
- thereby producing a smooth deposited film and substantially reducing or eliminating the need for volatile organic coalescent solvents.
Dependencies are inferred from the claim text.