Method of making cast-to-size epoxy tools for stamping sheet metal panels
AssigneeGeneral Motors Corporation
InventorsWilliam A. Martell, Ladislaus Weiss
Life of this patent
Estimating the term…
Abstract
Very large tools can be cast-to-size by making a pattern of the article to be formed by the tool, laying the pattern up in a pattern box, applying a release coat and coating the pattern and box with a tough, curable tool surface layer. A small amount of epoxy filled with a thermally conductive particulate filler is cast into the pattern box before the surface layer fully cures. Relatively large chunks of thermally conductive material are added to the box which are covered with additional cast epoxy. The cure of the epoxy is controlled to effect complete cure at room temperature within a few days but never to exceed a peak cure temperature above about 70.degree. C.
Claims7
A method of making a large, cast-to-size, epoxy tool comprising the steps of providing a pattern of the article to be formed by the tool;
- orienting said pattern in a pattern box;
- applying a release coating to the surfaces of the pattern and the box which define the surfaces of the tool;
- coating said surfaces with a thin layer of a tough curable tool surfacing compound;
- partially filling said pattern box with a liquid epoxy containing at least about 50 volume percent of thermally conductive particulate filler before said surfacing compound fully cures;
- adding at least about 30 volume percent of the tool volume of chunks of thermally conductive material to said liquid epoxy;
- filling said box with additional liquid epoxy to cover said chunks;
- and fully curing said epoxy and surfacing compound such that the internal temperature of the tool never exceeds about 70.degree. C., the presence of the thermally conductive filler and chunks serving to mediate heat generated by the epoxy exotherm to prevent run-away cure, shrink and shape change of the tool with respect to the pattern.
A method of making a large, cast-to-size, matched set of epoxy tools for forming sheet stock comprising the steps of providing a pattern of the article to be formed by the tool set;
- orienting said pattern in a pattern box;
- applying a release coating to the surfaces of the pattern and the box which define the surfaces of the first tool of the tool set;
- coating said surfaces with a thin layer of a tough curable tool surfacing compound;
- partially filling said pattern box with a liquid epoxy containing at least about 50 volume percent of thermally conductive particulate filler before said surfacing compound fully cures;
- adding at least about 30 volume percent of the tool volume of chunks of thermally conductive material to said liquid epoxy;
- filling said box with additional liquid epoxy to cover said chunks;
- and fully curing said epoxy and surfacing compound such that the internal temperature of the said first tool never exceeds about 70.degree. C., orienting the fully cured first tool in a second pattern box;
- applying a removable layer having the thickness of the sheet stock to be formed by the tool set to the surfaces of the cured first tool and the pattern box that define the working surface of the second tool of the set;
- applying a release coating to the surfaces of the removable layer and the second box which define the surfaces of the second tool;
- coating said surfaces for said second tool with a thin layer of a tough curable tool surfacing compound;
- partially filling said second pattern box with a liquid epoxy containing at least about 50 volume percent of thermally conductive particulate filler before said surfacing compound for the second tool fully cures;
- adding at least about 30 volume percent of chunks of thermally conductive material to said liquid epoxy;
- filling said second box with additional liquid epoxy to cover said chunks;
- and fully curing said epoxy and surfacing compound for said second tool such that the internal temperature of the second tool never exceeds about 70.degree. C., the presence of the thermally conductive filler and chunks serving to mediate heat generated by the epoxy exotherm to prevent run-away cure, shrink and shape change of the first and second tools of the tool set with respect to the pattern.
A method of making a large, cast-to-size epoxy tool comprising the steps of providing a pattern of the article to be formed by the tool;
- orienting said pattern in a pattern box;
- applying a release coat to the surfaces of the pattern and the box which define the surfaces of the tool;
- coating said surfaces with a thin layer of tough, curable tool surfacing compound;
- at least partially curing said compound;
- adding at least about 30 volume percent of the tool volume of chunks of thermally conductive material having high compressive strength;
- filling said pattern box with a liquid epoxy containing at least about 50 volume percent of a thermally conductive particulate filler;
- and fully curing said epoxy and surfacing compound such that the internal temperature of the tool never exceeds about 70.degree. C., the presence of the thermally conductive filler and chunks serving to mediate heat generated by the epoxy exotherm to prevent run-away cure, shrink and shape change of the tool with respect to the pattern.
Dependencies are inferred from the claim text.