Resin binders for foundry molding sands
AssigneeRohm Co., Ltd.
InventorsHeinz-Jochen Auer, Wolfgang Klesse, Peter Quis, Walther W. Szubinski
Life of this patent
Estimating the term…
Abstract
An aqueous dispersion of a copolymer comprising: (A) from 20 to 90 percent by weight of an unsaturated carboxylic acid of the formula ##STR1## where R.sub.1, R.sub.2, R.sub.3 are hydrogen, alkyl, or --(CH.sub.2).sub.n COOM and M is a proton or an alkali metal or alkaline earth metal or an ammonium cation, and (B) from 10 to 80 percent of at least one other comonomer different from and copolymerizable with A; methods of making a ready-to-use foundry molding sand by mixing such a dispersion with sand; and such ready-to-use foundry molding sands.
Claims17
A ready-to-use foundry molding sand composition which is a mixture of sand and such an amount of an aqueous dispersion containing from 10 to 60 percent by weight of a water insoluble synthetic resin copolymer that said mixture contains from 0.1 to 10 percent by weight of said copolymer, said copolymer comprising
- (A) from 20 to 90 percent by weight of an unsaturated carboxylic acid of the formula ##STR11## wherein R.sub.1, R.sub.2 and R.sub.3 are independently hydrogen, alkyl having from 1 to 6 carbon atoms, or --(CH.sub.2).sub.n --COOM, where M is a proton or an alkali metal or alkaline earth metal or an ammonium cation, and n is 0 or 1, but where no more than two --COOM groups are present in the acid molecule and where those groups --COOM wherein M is an alkali metal or alkaline earth metal cation are not more than 20 percent by weight of all --COOM groups present in said copolymer;
- and
- (B) from 10 to 80 percent by weight of at least one monomer different from and copolymerizable with (A).
A ready-to-use foundry molding sand composition which is a mixture of sand and such an amount of an aqueous dispersion containing about 10 to 60 percent by weight of a water insoluble synthetic resin copolymer that said mixture contains from 0.1 to 10 percent by weight of said copolymer, said copolymer comprising
- (A) from 20 to 90 percent by weight of an unsaturated carboxylic acid of the formula ##STR12## wherein R.sub.1, R.sub.2 and R.sub.3 are independently hydrogen, alkyl having from 1 to 6 carbon atoms, or --(CH.sub.2).sub.n --COOM, where M is a proton or an alkali metal or alkaline earth metal or an ammonium cation, and n is 0 or 1, but where no more than two --COOM groups are present in the acid molecule and where those groups --COOM wherein M is an alkali metal or alkaline earth metal cation are not more than 20 percent by weight of all --COOM groups present in said copolymer;
- and
- (B) from 10 to 80 percent by weight of one or more monomers different from and copolymerizable with (A) and having the same or different functional groups capable of non-radical addition of condensation crosslinking reaction with each other at a temperature above 60.degree. C.
A ready-to-use foundry molding sand composition which is a mixture of sand, such an amount of an aqueous dispersion containing from 10 to 60 percent by weight of a water-insoluble synthetic resin copolymer that said mixture contains from 0.1 to 10 percent by weight of said copolymer, and a multifunctional non-radically crosslinking agent for said copolymer, said copolymer comprising
- (A) from 20 to 90 percent by weight of an unsaturated carboxylic acid of the formula ##STR14## wherein R.sub.1, R.sub.2 and R.sub.3 are independently hydrogen, alkyl having from 1 to 6 carbon atoms, or --(CH.sub.2).sub.n --COOM, where M is a proton or an alkali metal or alkaline earth metal or an ammonium cation, and n is 0 or 1, but where no more than two --COOM groups are present in the acid molecule and where those groups --COOM wherein M is an alkali metal or alkaline earth metal cation are not more than 20 percent by weight of all --COOM groups present in said copolymer;
- and
- (B) from 10 to 80 percent by weight of one or more monomers different from and copolymerizable with (A) and having the same or different functional groups capable of non-radical addition or condensation crosslinking reaction with said multifunctional crosslinking agent at a temperature above 60.degree. C.
A ready-to-use foundry molding sand composition which is a mixture of said, such an amount of an aqueous dispersion containing from 10 to 60 percent by weight of a water insoluble synthetic resin copolymer that said mixture contains from 0.1 to 10 percent by weight of said copolymer, from 1 to 10 percent, by weight of said copolymer, of a radically crosslinking monomer having a boiling point of at least 150.degree. C., and from 0.1 to 5 percent, by weight of said crosslinking monomer, of a free radical polymerization initiator soluble in said radically crosslinking monomer, said copolymer comprising
- (A) from 20 to 90 percent by weight of an unsaturated carboxylic acid of the formula ##STR16## wherein R.sub.1, R.sub.2 and R.sub.3 are independently hydrogen, alkyl having from 1 to 6 carbon atoms, or --(CH.sub.2).sub.n --COOM, where M is a proton or an alkali metal or alkaline earth metal or an ammonium cation, and n is 0 or 1, but where no more than two --COOM groups are present in the acid molecule and where those groups --COOM wherein M is an alkali metal or alkaline earth metal cation are not more than 20 percent by weight of all --COOM groups present in said copolymer;
- and
- (B) from 10 to 80 percent by weight of at least one monomer different from and copolymerizable with (A).
Dependencies are inferred from the claim text.