Refractory fused chrome-alumina bricks and compositions made from a granular fused material and processes for their production
AssigneeDresser Industries, Inc.
InventorTeresa M. Fraser
Life of this patent
Estimating the term…
Abstract
A refractory composition that is highly resistant to siliceous slag comprising from 45-85 weight percent chromic oxide and 15-55 weight percent alumina, said composition having a coarse grain fraction of -4 mesh and a fine grain fraction of -325 mesh comprising 40-100 weight percent chromic oxide.
Claims6
A refractory composition consisting of from 45 through 85 weight percent chromic oxide, and 15 through 55 weight percent alumina, said composition consisting of a fused coarse grain fraction of -4 mesh and a fine grain fraction of -325 mesh forming a bonding matrix, said fine grain fraction comprising 40 through 100 weight percent chromic oxide.
A method of manufacturing a refractory brick having high resistance to siliceous slag comprising the steps of:
- providing a size graded batch having a coarse grain fraction of -4 mesh comprising 70 through 75 volume percent and a fine grain fraction of -325 mesh comprising 25 through 30 volume percent, said fine grain fraction comprising 40 through 100 weight percent chromic oxide, said batch consisting of from 45 through 85 weight percent chromic oxide and 15 through 55 weight percent alumina;
- mixing a bonding agent with the batch to obtain a formable mix;
- pressing the mix to form a brick-like shape;
- and
- drying and burning the shape to form said brick.
In a method for increasing the siliceous slag resistance of a chrome-alumina composition wherein the improvement comprises the steps of:
- providing a size graded batch of fused chrome and alumina including a -4 mesh coarse grain fraction and a -325 mesh fine-grain fraction;
- and
- adding sufficient quantities of fine grain chromic oxide to said fine grain fraction such that 40 through 100 weight percent of said grain fraction consists of chromic oxide.
A siliceous slag resistant brick consisting of 45 through 85 weight percent chromic oxide;
- and 15 through 55 weight percent alumina, said brick including a -4 mesh fused coarse grain fraction and a -325 mesh fine grain fraction, said fine grain fraction comprising 40 through 100 by weight percent chromic oxide.
Dependencies are inferred from the claim text.