Process for the production of an aqueous bituminous preparation
OwnerBelane Karacsonyi nee Eva Spindler, Bela Racz +3inventors
InventorsBelane Karacsonyi nee Eva Spindler, Bela Racz, Istvan Boszormenyi, Laszlo Kiraly, Andras Medgyesi
Life of this patent
Estimating the term…
Abstract
A stable, thixotropic aqueous bitumen dispersion containing no emulsifier is prepared. Alkaline earth metal hydroxide and an aluminum salt are brought into contact to form an aqueous aluminum hydroxide gel. Molten bitumen is dispersed in the gel. The dispersion has a good shelf life and is stable with respect to electrolytes and chemically active construction materials.
Claims10
A process for preparing a stable, thixotropic aqueous bitumen dispersion without emulsifier, which comprises contacting an alkaline earth metal hydroxide and an aluminum salt wherein the amount of alkaline earth metal hydroxide is in excess of that which is stoichiometrically required for forming aluminum hydroxide, and dispersing from about 35% to about 65% (wt), based on the dispersion, of molten bitumen in an aqueous aluminum hydroxide dispersion, the aqueous dispersion further containing the aforesaid excess of unreacted alkaline earth metal hydroxide, whereby the resulting dipersion has a good shelf life and is stable with respect to electrolytes and chemically active construction materials.
A process for the production of an aqueous bitumen dispersion without emulsifier, which comprises preparing an aqueous aluminum hydroxide gel by the reaction in water of aluminum sulfate and calcium hydroxide in a weight ratio of 1:3 to 1:10 and while the aluminum hydroxide gel is still relatively fresh, dispersing from about 35% to about 65% (wt) based on the dispersion, of bitumen in said aqueous reaction mixture at a temperature above the softening point of bitumen, whereby a thixotropic dispersion is obtained that is stable with respect to electrolytes and chemically active construction materials.
A stable, aqueous, thixotropic bituminous dispersion that is free of emulsifiers, which comprises from about 35% to about 65% (wt) bitumen suspended in water with the aid of an aluminum hydroxide suspending agent, said suspending agent having been prepared relatively soon before the bitumen was suspended, by a reaction between an aluminum salt and an alkaline earth metal hydroxide, with the latter being in excess of that stoichiometrically required for the reaction with the aluminum salt, the dispersion further comprising the aforesaid excess of the alkaline earth metal hydroxide, whereby the resulting dispersion has a good shelf life and is stable with respect to electrolytes and chemically active construction materials.
An aqueous bitumen dispersion without emulsifier, which comprises from about 35% to about 65% (wt) bitumen suspended in water with the aid of an aluminum hydroxide gel made in situ by the reaction in water of aluminum sulfate and a stoichiometric excess of calcium hydroxide in a weight ratio of 1:3 to 1:10, the suspension further containing the excess calcium hydroxide and calcium sulfate formed from the said reaction, whereby said dispersion is thixotropic and is stable with respect to electrolytes and chemically active construction materials.