Process for adhering polyurethane elastomer to metal
AssigneesMitsubishi Chemical Industries Limited, Ihara Chemical Industry Co., Ltd.
InventorsMasaaki Ohtani, Takao Harada, Yoshijiro Oyaizu, Tatsuhiko Kobayashi
Life of this patent
Estimating the term…
Abstract
A polyurethane elastomer and a metal are strongly adhered by using (1) a composition containing a polyepoxy compound and a polyamine compound and (2) a composition containing an isocyanate compound having a concentration of isocyanate group of 15-50% by weight. An adhered composite article thus obtained has excellent water resistance and heat resistance.
Claims7
A process for adhering polyurethane elastomer to metal, which comprises:
- coating the surface of the metal with a composition-A containing a polyepoxy compound, a polyamine compound and a silane coupling agent;
- drying the thus coated surface of the metal;
- further coating the dried surface of the metal with a composition-B containing an isocyanate compound having a concentration of isocyanate groups of 15-50% by weight and at least one compound selected from the group consisting of polyester and polyurethane, each having a weight average molecular weight of more than 10,000;
- drying the thus double-coated surface of the metal;
- casting a raw material for a polyurethane elastomer onto the thus dried surface of the metal;
- and
- hardening said cast raw material.
A process for adhering polyurethane elastomer to metal, which comprises:
- coating the surface of the metal with a composition-A containing a polyepoxy compound, a polyamine compound selected from the group consisting of diethylenetriamine, tetraethylenepentamine, hexamethylenediamine, propylenediamine, trimethylhexamethylenediamine, isophoronediamine, menthenediamine, xylylenediamine, the reaction product of one of said polyamines with an epoxy compound, an amino group containing compound formed by the reaction of a dicarboxylic acid and a polyamine, a compound formed by the reaction of formaldehyde, a phenolic compound and a secondary amine and a polyamine obtained by the reaction of an aromatic amine and an aldehyde, and a silane coupling agent;
- drying the thus coated surface of the metal;
- further coating the dried surface of the metal with a composition-B containing an isocyanate compound having a concentration of isocyanate groups of 15-50% by weight and at least one compound selected from the group consisting of polyester and polyurethane, each having a weight average molecular weight of more than 10,000;
- drying the thus double-coated surface of the metal;
- casting a raw material for a polyurethane elastomer onto the thus dried surface of the metal;
- and
- hardening said cast raw material.
A composite article of an adherent elastomer layer on a metal substrate obtained by a process, comprising:
- coating the surface of the metal with a composition-A containing a polyepoxy compound, a polyamine compound and a silane coupling agent;
- drying the coated surface of the metal;
- further coating the dried surface of the metal with a composition-B containing an isocyanate compound having a concentration of isocyanate groups of 15-50% by weight and at least one compound selected from the group consisting of polyester and polyurethane, each having a weight average molecular weight of more than 10,000;
- drying the thus double-coated surface of the metal;
- casting a raw material for a polyurethane elastomer onto the dried isocyanate layer of the metal;
- and
- hardening said cast raw material.
Dependencies are inferred from the claim text.