Preparation of cellulose acetate membrane and its use for polar solvent-oil separation
AssigneeExxon Research & Engineering Co.
InventorDavid L. Wernick
Life of this patent
Estimating the term…
Abstract
It has been discovered that cellulose acetate membranes, fabricated using nonaqueous solvent systems, can be used for the separation of polar solvents, especially ketone dewaxing solvents from dewaxed oil. The cellulose acetate membranes so prepared are of a reduced acetyl content and exhibit very good resistance to ketone solvents. The specific fabrication procedure avoids exposing the cellulose acetate to even transient mixtures of ketone and alcohol or ketone and water. Although the cellulose acetate polymer is insoluble in pure water, alcohol, or ketone it is soluble in mixtures of ketone-alcohol and ketone-water. The resulting membrane is an effective means for separating ketone dewaxing solvent from dewaxed oil.
Claims3
A method for producing a cellulose 1.7-1.8 acetate membrane comprising:
- (a) dissolving 5 to 40 weight percent cellulose 1.7-1.8 acetate polymer in a dual casting solvent system comprising 15 to 50 weight percent solvent A and 20 to 80 weight percent solvent B wherein solvent A is more volatile than solvent B and wherein solvent B is a nonsolvent for the polymer while solvent A is either a solvent or nonsolvent for the polymer, but the mixture A plus B is a solvent for the polymer;
- (b) casting a film using the solution of step (a);
- (c) evaporating a portion of the more volatile solvent A from the film;
- and
- (d) gelling the partially evaporated film in a gelation solvent C which does not dissolve the polymer but is miscible with solvents A and B and further wherein the solvent combination of B+C is a nonsolvent for the polymer, wherein solvent A possesses three dimensional solubility parameters in the range of .delta..sub.D =7 to 10, .delta..sub.P =1 to 10 and .delta..sub.H =6 to 12 and solvents B and C possess three dimensional solubility parameters in the range of .delta..sub.D =7 to 10, .delta..sub.P =0 to 10 and .delta..sub.H <2.5, wherein all .delta.'s are in (cal/cm.sup.3).sup.1/2.