Process for manufacturing a motor vehicle windshield
AssigneeSocieta Italiana Vetro - SIV - S.p.A.
InventorFrancesco Sebastiano
Life of this patent
Estimating the term…
Abstract
Process for manufacturing a safety motor vehicle windshield, more especially as regards lower formation of glass fragments in the event of impact or fracture of said windshield. The process consists in coating the inside surface of said windshield with a liquid composition, which, after curing with ultraviolet and infrared rays, from a high strength, hard and flexible film. The coating is prepared so that, during the curing process, a polyurethane of aliphatic polycaprolactone is formed as an interpenetrating network system, with a partially crosslinked vinylacrylic copolymer, the whole being formed in the presence of a controlled quantity of a polyester urethane acrylate prepolymer.
Claims3
Process for manufacturing a safety glass windshield for motor vehicles, said windshield having an appreciably lower formation of glass fragments or needles in the event of impact or fracture of the windshield which consists of:
- (A) coating a laminated glass windshield comprising two glass sheets bonded together with an intermediate plastic sheet on the clean inside surface of said windshield with a liquid composition consisting of the following components:
- (a) a linear polycaprolactone with a molecular weight between about 800 and 1200, and
- (b) an aliphatic polyisocyanate in an amount such as to be able to react with 95-100% of the hydroxyl groups present in the aforesaid polycaprolactone, and
- (c) vinyl and acrylic ester monomers, capable of providing a clear solution of the above mixed ingredients, wherein 10 to 35% of their total weight consists of a di- or tri-acrylate ester, and
- (d) a prepolymer formed from a linear polyester pre-reacted with an hydroxy-acrylate ester and an aliphatic isocyanate, such that the amount of said polymer is between 5 and 15% of the total composition, and
- (e) a photoinitiator, being 2-hydroxy-2-methyl-1-phenyl-propan-1-one in an amount of 1 to 3% of the total composition, and
- (f) with or without additives to control the flow properties of the liquid composition, and
- (B) curing said coated windshield to produce a polymerized film thereon, said film containing urethanes and vinyl-acrylate polymers, and components being employed in such proportions that the ratio of total urethanes to the total vinyl-acrylate polymers in the film is in the range of 1.3:1 to 1.0:1.
Dependencies are inferred from the claim text.