Cast iron with spheroidal graphite and austenitic-bainitic mixed structure
AssigneeHorst Muhlberger
InventorsHorst Muhlberger, Bruno Prinz, Wolf Wunder, Ulrich Schafer, Josef Bognar
Life of this patent
Estimating the term…
Abstract
A high ductility machinable cast iron with mixed austenitic-bainitic structure is made by a method which involves limiting the manganese content to less than 0.3% by weight and utilizing a substantially lower temperature austenitizing heat treatment (820.degree. to 830.degree. C.) for a shorter period (10 to 25 minutes) than has hitherto been considered to be necessary to achieve such structures. The low alloy cast iron can therefore be made from available scrap with low manganese content and at low cost.
Claims3
A method of making a cast iron of mixed austenitic-bainitic structure, which consists essentially of the steps of:
- forming a spheroidal graphite cast iron composition containing 0.01 to 0.25% by weight manganese, 0.1 to 1.5% by weight copper, 2.5 to 3.9% by weight carbon, 2.0 to 3.0% by weight silicon, 0.2 to 0.8% by weight molybdenum, 0.01 to 3% by weight nickel, and the balance iron;
- subjecting the cast iron to an austenitic heat treatment for 10 to 25 minutes at a temperature of 820.degree. to 830.degree. C.;
- rapidly cooling the resulting austenitized cast iron to a temperature of substantially 350.degree. to 400.degree. C. over a period of less than 2 minutes;
- and
- holding the cast iron after the rapid cooling at the latter temperature for a period of 5 to 60 minutes, thereby forming a readily machinable product contrasting with cast irons containing more than 0.3% by weight manganese by reduced hardness and greater ductility.