AssigneeHenkel Kommanditgesellschaft auf Aktien
InventorsNorbert Maak, Wolfgang Friedemann, Hans Fehr, Kurt Feulner
Life of this patent
Estimating the term…
Abstract
Aqueous alkali metal silicate bonding compositions having a molar ratio of SiO.sub.2 :Me.sub.2 O of 2.4:1 to 3.4:1, wherein Me is sodium and/or potassium, a solids content of about 35 to 50 percent by weight, and containing triethanolamine. The bonding compositions can be mixed with fillers such as quartz sand and used for the manufacture of molded forms for the casting of metals.
Claims10
A process for forming a foundry core or mold component comprising the steps of
- (I) forming a mixture of
- (a) from about 3 to about 6 percent by weight of a pre-formed aqueous bonding solution comprising
- (A) an alkali metal silicate solution having a molar ratio of SiO.sub.2 :Me.sub.2 O of from about 2.4:1 to about 3.4:1, wherein Me represents sodium and/or potassium and a solids content of from about 35 to about 50% by weight, based on the weight of the alkali metal silicate solution;
- and
- (B) from about 0.1% by weight to the solubility limit in the aqueous alkali metal silicate solution of triethanolamine;
- and
- (b) from about 94 to about 97 percent by weight of a finely divided filler material;
- (II) shaping the mixture formed in (I) into the shape of a core or mold component;
- and
- (III) curing the shaped mixture.
7 more elements
A process for forming a foundry core or mold component comprising the steps of
- 1. forming an aqueous alkali metal silicate bonding composition by mixing together
- (i) an aqueous alkali metal silicate solution wherein the alkali metal silicate has a molar ratio of SiO.sub.2 :Me.sub.2 O of from about 2.4:1 to about 3.4:1 wherein Me represents sodium and/or potassium, and the solution has a solids content of from about 35 to about 50 percent by weight, based on the weight of the solution,
- (ii) from about 0.1 percent by weight to the solubility in the aqueous alkali metal silicate solution in (i) of triethanolamine, based on the weight of the aqueous alkali metal silicate bonding composition, and optionally,
- (iii) one or more of the following ingredients a solubility enhancer;
- an anionic surfactant;
- a nonionic surfactant;
- a carbohydrate;
- and a lithium silicate;
- 2. mixing from about 3 to about 6 percent by weight of the aqueous alkali metal silicate bonding composition formed in Step (1.) above with from about 97 to about 94 percent by weight of a finely divided filler material;
- 3. shaping the mixture formed in Step (2.) above into a foundry core or mold;
- and
- 4. curing the shaped mixture.
9 more elements