Method of producing low temperature cure latexes

In a process for producing an aqueous coating composition comprising a glycoluril derivative and a reactive aqueous emulsion polymer wherein the coating composition is adapted to be heat cured to cross-link the glycoluril derivative with the reactive aqueous emulsion polymer, the improvement comprising:

• heat reacting an aqueous polymeric mixture comprising by weight between about 5% and 55% glycoluril derivative and between 45% and 95% of a preformed reactive aqueous emulsion polymer at temperatures between about 60.degree. C. and 90.degree. C. for time sufficient less than two hours to partially heat react said glycoluril derivative with said reactive aqueous emulsion polymer to provide a minor amount of coreaction between the glycoluril derivative and the reactive aqueous emulsion polymer without gelling the polymeric mixture, the reactive aqueous emulsion polymer containing reactive hydroxyl, carboxyl, or acrylamide groups for coreacting with said glycoluril derivative.