Process for making foamed, sulfur-cured polymer blend compositions
AssigneeE. I. Du Pont de Nemours and Company
InventorGary L. Loomis
Life of this patent
Estimating the term…
Abstract
A blend of an E/X/Y copolymer, where E is ethylene, X is a vinyl ester, and Y is carbon monoxide or sulfur dioxide, with a polymer of vinyl halide or vinylidene halide is foamed and cured by dispersing in the blend a blowing agent and sulfur or a sulfur-releasing agent and heating the blend containing those additives at 100.degree.-180.degree. C. for a sufficient time to produce curing and foaming. This process can be run either continuously or batchwise in conventional equipment under conventional conditions in the presence of air. Plasticizers and other materials which often interfere with peroxide cures can be present in the process of this invention. The foamed and cured products have excellent physical properties and ozone resistance.
Claims9
A process for producing a foamed, cured composition comprising a polymer blend of
- (1) 5 to 95 parts of E/X/Y copolymer, wherein
- E is ethylene;
- X is a vinyl ester;
- and
- Y is carbon monoxide or sulfur dioxide;
- and
- (2) 95 to 5 parts of a polymer of a vinyl halide or vinylidene halide, the total amont of polymers (1) plus (2) being 100 parts;
- said process comprising:
- (A) uniformly dispersing in said polymer blend an effective amount of a blowing agent and at least one curing agent selected from
- (a) about 0.2 to 5 parts of sulfur and (b) about 0.2 to 15 parts of an agent capable of releasing elemental sulfur under the cure conditions;
- and
- (B) heating said blend containing the blowing agent and the curing agent at a temperature of about 100.degree.-180.degree. C., at which both foaming and curing take place, for a sufficient time to obtain substantially complete foaming and curing.
A process of claim 4 wherein the curing agent is sulfur.
Dependencies are inferred from the claim text.