Metal-backed layered composite and method of making same
AssigneeGlyco-Metall-Werke Daelen & Loos GmbH
InventorsKarl-Heinz Wegner, Erich Hodes, Horst Mann
Life of this patent
Estimating the term…
Abstract
A composite material for use as shock absorber, as bushings or the like having controlled friction characteristics of a layer bonded to a metal substrate is formed by applying a particulate composition of a thermoplastic synthetic resin and carbon fibers having a maximum length of 1 mm to the substrate and heating it to a temperature of 50.degree. to 70.degree. K. above the melting temperature of the synthetic resin.
Claims13
A composite material comprising:
- a metal substrate having a roughened surface and
- a facing layer bonded to said surface of said substrate, said facing layer comprising:
- a thermoplastic synthetic resin matrix composed of a polyether-etherketone as the sole resin, and
- as the sole reinforcement in said matrix, short graphite fibers dispersed therein and having a length of substantially 0.04 mm to 0.2 mm and a diameter of substantially 0.005 mm to substantially 0.03 mm, said carbon fibers making up substantially 20 to 45% by weight of said layer.
A method of making a composite material which comprises the steps of:
- (a) preparing a composition of particles of a matrix-forming polyether-etherketone thermoplastic synthetic resin having a particle size of at most 100 microns, and short graphite fibers having a length of at most 1 mm by milling the thermoplastic synthetic resin in liquid nitrogen to said particle size, then adding the graphite fibers to the milled resin, and blending said graphite fibers in the milled resin to form said composition such that said graphite fibers are incorporated in said composition in an amount of 20 to 40% by weight and have a length of substantially 0.04 mm to 0.2 mm and a diameter of 0.005 mm to 0.03 mm;
- (b) applying the prepared composition to a roughened surface of a metallic substrate and doctoring said composition onto said surface to form a layer of uniform thickness thereon;
- (c) heating said layer to a temperature of substantially 50.degree. to 70.degree. K. above the melting point of the thermoplastic of said layer to transform said layer into a homogeneous coating on said substrate;
- and
- (d) cooling said substrate.
The method defined in claim 11 wherein the mechanically roughened surface is degreased.
Dependencies are inferred from the claim text.