Intramolecular polymer complexes - viscosifiers for high ionic strength drilling fluids
AssigneeExxon Research & Engineering Co.
InventorsDennis G. Peiffer, Robert D. Lundberg, Thad O. Walker, S. Richard Turner
Life of this patent
Estimating the term…
Abstract
A new family of terpolymers based on acrylamide/sodium styrene sulfonate/methacrylamidopropyltrimethylammonium chloride has been found to be an improved viscosity control additive for water-based drilling muds. The resultant muds display good viscosity characteristics, thermal stability and gel strength when formulated from the terpolymer intramolecular complex having the appropriate polymer concentration and salt level.
Claims5
A drilling mud which comprises:
- (a) salt water having about 0.1 to about 50 grams of salt per 100 ml. of water;
- (b) about 4 to about 30 lbs/bbl of clay;
- (c) about 1 to about 30 lbs/bbl of a lignosulfonate;
- (d) weighting material of sufficient quantity necessary to achieve the desired density;
- (e) about 0.25 to about 5 lbs/bbl of a terpolymer having the formula:
- ##STR2## wherein x is about 40 to about 98 mole %, y is about 1 to about 50 mole %, z is about 1 to about 50 mole percent, wherein y and z are less than 60 mole %, and M is selected from the group consisting of amines and a metallic cation being selected from the group consisting of lead, iron, aluminum, Groups IA, IIA, IB and II of the Periodic Table of Elements, the molecular weight of said terpolymer as measured by intrinsic viscosity being 1.times.10.sup.3 to 5.times.10.sup.6 ;
- and
- (f) base of sufficient quantity to adjust the pH of the water-based drilling mud to about 10 to about 10.5.
5 more elements
A drilling mud which comprises:
- (a) salt water having about 0.1 to about 50 grams of salt per 100 grams of water;
- and
- (b) about 0.25 to about 15 lbs/bbl of the acrylamide-based polyampholyte containing low to moderate levels of anionic and cationic groups to increase the viscosity of said drilling mud, said terpolymer containing acrylamide monomer units and having about 1 to about 50 mole % of the charged monomer units, said terpolymer possessing unequal molar ratio of anionic and cationic monomers, said anionic monomer being sodium styrene sulfonate, and said cationic monomer being selected from the group consisting of methacrylamidopropyltrimethylammonium chloride, dimethyldiallylammonium chloride, diethyldiallylammonium chloride, 2-methacryloxy-2-ethyltrimethylammonium chloride, trimethylmethacryloxethylammonium methosulfate, 2-acrylamido-2-methylpropyltrimethylammonium chloride, and vinylbenzyltrimethylammonium chloride.
Dependencies are inferred from the claim text.