Abstract
A method of enhancing the corrosion resistance of sintered stainless steel, particularly against attack by acids, such as acetic acid, under non-oxidizing conditions. The sintered stainless steel is activated, for example by treatment with acid and is then treated with a phosphate containing solution. The sintered stainless steel has improved resistance to subsequent attack by acid.
Claims9
A process for the treatment of a sintered stainless steel element to enhance its corrosion resistance, the element being porous having pores with interior surfaces and for use in an environment in which aqueous acetic acid solution will be passed through the element, said process comprising the steps of:
- (a) passing a preliminary flow of an aqueous acetic acid solution through the element in an amount sufficient to at least partially activate the interior surfaces of pores in the elements,
- (b) terminating the preliminary flow of acetic acid, then
- (c) passing a flow of a phosphate containing solution through the element within a period of time short enough after terminating the flow of acid to prevent excessive accumulation of corrosion products within the pores to generate a corrosion resistant coating on the previously activated interior surfaces of the element, and
- (d) terminating the flow of phosphate containing solution,
- (e) said corrosion resistant coating being effective to resist corrosion by subsequent flows of aqueous acetic acid solution through the element.
A method of inhibiting corrosion in a porous, sintered stainless steel element having interior surfaces wherein the element is subject in use to corrosive acidic solutions, said method comprising the steps of:
- (a) passing a non-oxidizing acidic solution through the porous element to deplete any oxide layer present on the interior surfaces,
- (b) terminating the passage of the acidic solution, and then
- (c) passing a phosphate containing solution through the element to form a passivating phosphate layer on the interior surfaces, and then
- (d) again passing the acidic solution through the element.