Abstract

A metal or metal compound coating 6 is deposited on a face of a hot, freshly formed ribbon 1 of glass during the ribbon's forward travel through a coating station 5 between a forming installation 3 and an annealing lehr 4 by contacting the ribbon face with fluid coating precursor material e.g. sprayed from nozzle 17. Preparatory to the coating step, the ribbon 1 is passed through successive thermal conditioning zones comprising a zone 19 in which temperature gradients across the ribbon are reduced and a following zone in which heat is supplied substantially entirely to a surface layer of the glass at the face to be coated by exposing that face to one or more radiant heaters 22 having a black body temperature below 1100.degree. C. to compensate at least partially for the cooling effect of the coating step on the ribbon 1.

Claims8

Dependent claims

A process for producing flat glass coated on one side with a coating comprised of one of a metal and a metal compound, wherein the glass is formed in a flat glass forming installation and subsequently annealed in an annealing installation, said process comprising:

advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation;
passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon;
passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated;
contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon;
and wherein
said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100.degree. C. to compensate at least partially for the cooling effect of said contacting step, and
said process further comprises monitoring the temperature of the ribbon surface at the coated side after said contacting step;
and controlling the at least one radiant heater so that the coated side complies with predetermined temperature conditions prior to entering the annealing installation.

5 more elements

advancing a freshly formed ribbon of hot flat glass from the flat glass forming installation to the annealing installation;
passing the ribbon through a first thermal conditioning zone located downstream of the glass forming installation for reducing temperature gradients across the ribbon;
passing the ribbon through a second thermal conditioning zone located downstream of the first thermal conditioning zone for supplying heat substantially entirely to a surface layer of the glass at the one side to be coated;
contacting the one side of the advancing glass with a fluid medium which includes substances from which the coating is formed, said contacting step being performed at a coating station located between the second thermal conditioning zone and the annealing installation and having a cooling effect upon the advancing ribbon;
and wherein
said step of passing the ribbon through the second thermal conditioning zone includes supplying the heat with the use of at least one radiant heater having a black body temperature below 1100.degree. C. to compensate at least partially for the cooling effect of said contacting step, and
said process further comprises monitoring the temperature of opposite points on the respective surfaces of the ribbon after said contacting step;
and controlling the at least one radiant heater in dependence upon any difference between the temperatures of such opposite points.

5 more elements