US 4,529,863 AGranted

Gas metal arc welding method

AssigneeP.P.I. Performance Process International

InventorJean-Claude Lebel

Life of this patent

Estimating the term…

Loading patent…

Abstract

A gas-metal-arc welding method is provided for high speed, high melting rate, substantially spatter-free, all-position welding. The method is particularly useful for out-of-position welding, that is, to produce vertical, inclined and overhead welds. A consumable wire electrode is held within and fed through the tubular contact tip of a continuous feed type welding gun having a tubular nozzle surrounding and extending beyond the tip. A shielding gas, formed of unique ratios of a minor proportion of a carbon dioxide and oxygen mixture combined with a major proportion of an argon and helium mixture, is flowed in a substantially longitudinally laminar pattern between the nozzle and contact tip and along the electrode extension from the tip. The contact tip is cooled, and sufficiently high power electrical current is passed through the contact tip and electrode extension to produce the arc and to melt the end of the electrode into molten drops for short-circuiting (e.g., low current) or for spray (e.g., higher current) transfer of the drops to the weld deposit. The electrode extension is pre-heated by maintaining a long electrode extension or stick-out beyond the contact tip end, with a substantial portion of the extension recessed within the nozzle.

A gas-metal-arc welding method for substantially spatter-free, high melting rate welding, useful for out-of-position welding of ferrous metals using a consumable, wire electrode held in a contact tip of a continuous feeding type, gas-metal-arc welding gun for continuously advancing the electrode longitudinally towards a weld deposit, with an electrode end positioned adjacent to, for forming an arc gap with, a weld pool deposit location, comprising the steps of:

flowing through the electrode an electrical current of sufficient, predetermined amperage and voltage to melt the electrode and for forming molten drops thereon which are deposited upon the weld pool;
pre-heating and increasing the melting rate of the electrode by continuously maintaining a relatively long electrode extension beyond the contact tip;
continuously flowing a substantially longitudinally laminar stream of gas around the contact tip, the electrode extension and the gap, with said gas comprising a major proportion of an argon and heium mixture and a minor proportion of a carbon dioxide and oxygen mixture,
and transferring the molten drops to the weld pool by either short-circuiting the drops to the pool for inclusion of the drops in the pool for out-of-position or flat position welding or alternatively, by spray transfer deposition of the drops from the electrode end to the pool when welding in the flat position only;
and
the approximate volumetric relationships of the gases being calculated as:
(1) carbon dioxide between about 2.5-8.5%, oxygen between about 0.1-0.8%, helium between about 25-60%, and argon the remainder, and
(2) with the ratio between carbon dioxide and oxygen being at approximately 10:1 to about 20:1;
(3) and with the oxidation potential relationship of the shielding gas calculated as the sum of the percent oxygen and 1/4 of the percent carbon dioxide, being between about 0.96 to 2.4;
(4) and with the percentage amount of helium in the total gas being calculated as being approximately 72.65 minus 5.65 times the percent of the carbon dioxide.