Method for coating quartz with boron nitride
AssigneeGeneral Electric Company
InventorRobert S. Lewandowski
Life of this patent
Estimating the term…
Abstract
A method for coating quartz with a protective boron nitride film constitutes heating the quartz member to a temperature of 900.degree. C. to 1000.degree. C. in a stream of inert gas. After heating the quartz member to the desired temperature, the flow of inert gas is discontinued, whereupon ammonia and diborane gases, mixed at a temperature of 200.degree. C. to 400.degree. C., are allowed to flow past the quartz member. The flow of mixed ammonia and diborane gases is maintained for a time sufficient to deposit a boron nitride film of desired thickness. The boron nitride is produced by chemical reaction between ammonia and diborane.
Claims6
A method for coating a quartz member with protective nitride film, said method comprising the steps of:
- heating said quartz member in a furnace having an inert gas flowing therethrough for a time sufficient for said quartz member to reach a temperature between about 900.degree. C. and 1,000.degree. C.;
- mixing at a temperature between about 200.degree. C. and 400.degree. C. ammonia gas and diborane gas, and initiating flow of the mixed ammonia and diborane gases past said quartz member when said quartz member has reached said temperature between about 900.degree. C. and 1,000.degree. C. and after discontinuing flow of said inert gas;
- and
- allowing said mixed ammonia and diborane gases to flow past said quartz member for a time sufficient to coat said quartz member with boron nitride film of desired thickness, said boron nitride being the product of a chemical reaction between said ammonia and diborane gases.
A method of applying a protective boron nitride film to the interior of a quartz tube, said method comprising the steps of:
- heating said quartz tube to between about 900.degree. C. and 1000.degree. C., and purging the interior of said tube with inert gas;
- mixing at a temperature of between about 200.degree. C. and 400.degree. C. ammonia gas and diborane gas and initiating flow of the mixed ammonia and diborane gases through the interior of said quartz tube when the temperature of said quartz tube has reached said temperature of between about 900.degree. C. and 1000.degree. C. and after discontinuing flow of said inert gas;
- and
- allowing said mixed ammonia and diborane gases to flow through said quartz tube for a time sufficient to coat the interior of said quartz tube with a boron nitride film of desired thickness, said boron nitride being the product of a chemical reaction between said ammonia and diborane gases.
Dependencies are inferred from the claim text.