High specific surface area carbides and nitrides
AssigneeBoard of Trustees of Leland Stanford Jr. Univeristy
InventorsMichel Boudart, Shigeo T. Oyama, Leo Volpe
Life of this patent
Estimating the term…
Abstract
Method and compositions produced thereby concerning high specific surface area carbides and nitrides. The carbides and nitrides are obtained by thermal reduction of oxides in the presence of a source of carbon or nitrogen respectively, with relatively slow progressive temperature increases prior to completion of the reaction, followed by quenching.
Claims12
A method for preparing high specific surface area molybdenum and vanadium carbides and nitrides from an oxide, said carbides and nitrides having at least a 5-fold increase in surface area over said oxide,
- which method comprises:
- in a first heating, heating said oxide to a temperature prior to significant reduction and formation of said carbide or nitride;
- in a second heating following said first heating, continuing heating of said oxide substantially uniformly and continuously at a rate in the range of about 0.1.degree. to 5.degree. K./min in the presence of a reducing environment and a source of carbon or nitrogen from a time at least 20 minutes prior to the time of completion of formation of said carbide or nitride and at a temperature at least 25.degree. K. prior to substantial completion of formation of said carbide or nitride, and through a temperature range where reduction of said oxide and reaction with carbide and nitrogen occurs to form a carbide or nitride respectively, said heating continuing until said reaction is substantially complete as evidenced by the substantial absence of change in the effluent composition;
- and
- quenching the reaction by lowering the temperature within the lesser of about one hour or about 50 percent of the time of said second heating.
A method for preparing a high specific surface area molybdenum or vanadium carbide from an oxide, said carbide having at least a 5-fold increase in surface area over said oxide,
- which method comprises:
- in a first heating, heating said oxide to a temperature prior to significant reduction and formation of said carbide;
- in a second heating following said first heating, continuing heating of said oxide substantially uniformly and continuously at a rate in the range of about 0.1.degree. to 5.degree. K./min in the presence of a reducing environment and a source of carbon from a time at least 20 minutes prior to the time of completion of formation of said carbide and at a temperature at least 25.degree. K. prior to substantial completion of formation of said carbide, and through a temperature range where reduction of said oxide in reaction with carbon occurs to form a carbide, said heating continuing until said reaction is substantially complete as evidenced by the substantial absence of change in the effluent composition;
- and
- quenching the reaction by lowering the temperature within the lesser of about one hour or about 50 percent of the time of said second heating.
A method for preparing high specific surface area molybdenum and vanadium nitrides from an oxide, said nitrides having at least a 5-fold increase in surface area over said oxide,
- which method comprises:
- in a first heating, heating said oxide to a temperature prior to significant reduction and formation of said nitride;
- in a second heating following said first heating, continuing heating of said oxide substantially uniformly and continuously at a rate in the range of about 0.1 to 5%/min in the presence of a gaseous source of hydrogen and nitrogen from a time at least 20 minutes prior to the time of completion of formation of said nitride and at a temperature at least 25.degree. K. prior to substantial completion of formation of said nitride, and through a temperature range where reduction of said oxide in reaction with nitrogen occurs to form a nitride, said heating continuing until said reaction is substantially complete as evidenced by the substantial absence of change in the effluent composition;
- and
- quenching the reaction by lowering the temperature within the lesser of about one hour or about 50 percent of the time of said second heating.