Epoxy resin coating compositions for printed circuit boards
AssigneeKollmorgen Technologies Corporation
InventorsEdward J. Leech, Frank D. Russo
Life of this patent
Estimating the term…
Abstract
A resinous protective coating useful in adhering plastics to metallic substrates. The protective coating is particularly useful as a solder mask and in the manufacture of printed circuit boards with circuit patterns having a resolution of at least 0.25 mm lines and spaces thereon. The protective coating comprises resins dissolved in solvents, wherein the coating, upon being subjected to heat, goes from a liquid or soft "gel-like" state into a solid phase without bleeding. The protective coating is resistant to copper, nickel and gold electroplating baths, adheres to insulating substrates, adhesive coated base materials as well as metallic substrates and is capable of withstanding the thermal shock of dip soldering.
Claims18
In a permanent, protective coating composition useful in the manufacture of printed circuit boards, said coating composition comprised of a thermosetting epoxy resin and curing composition dissolved in a solvent;
- and a flow promoter;
- said curing composition present in an amount sufficient to effect substantially complete cure of said thermosetting resin, said coating composition being in an initial state as a high viscosity solution and having an apparent viscosity between about 10,000 centipoise and about 200,000 centipoise, said coating composition upon curing, being transformed from said initial state into a final state as a solid, the improvement which comprises:
- said composition further including a thickening agent in an amount sufficient to gel said high viscosity solution into a soft gel-like initial state, said composition, upon curing, being transformed from said soft gel-like initial state directly into a cross-linked solid;
- said thermosetting epoxy resin being a solid at room temperature, having a melting point between 60.degree. C. and about 200.degree. C., and having an epoxide functionality greater than about 3;
- said curing composition including:
- a primary curing agent comprised of an alicyclic polyamine which is corrosive to copper surfaces, the primary curing agent being present in an amount sufficient to effect substantially complete cure of the thermosetting epoxy resin;
- and
- a secondary curing agent comprised of an aromatic amine, said secondary curing agent being present in an amount sufficient to provide said cured coating composition with resistance to flux removal processes.
A permanent, protective coating composition for use in the manufacture of printed circuit boards, said composition comprising:
- an epoxy resin dissolved in a solvent, said epoxy resin being a solid at room temperature, having an epoxide functionality more than about 3 and less than about 10, and having a melting point between about 60.degree. C. and about 200.degree. C.;
- a screening aid comprised of an epoxy resin which is liquid at room temperature;
- a flow promoter comprised of acrylate polymers and/or silicone;
- a toughener comprised of a liquid acrylonitrile polybutadiene and/or a solid epoxy resin having an epoxy equivalent weight above about 350;
- a primary curing agent comprised of an alicyclic polyamine which is corrosive to copper surfaces, said curing agent being present in an amount sufficient to effect substantially complete cure of said coating composition, said coating composition upon being cured transforming a high viscosity solution having an apparent viscosity between about 10,000 centipoise and about 200,000 centipoise into a solid;
- and
- a secondary curing agent comprised of an aromatic amine, said secondary curing agent being present in an amount sufficient to provide said cured coating composition with resistance to flux removal processes;
- a thickening agent in an amount sufficient to gel said high viscosity solution into a soft gel-like phase, said coating composition upon being cured transformed from said soft gel-like phase directly into a solid;
- and
- an organic acid in an amount sufficient to reduce or eliminate the basicity of the alicyclic polyamine in said protective coating composition while retaining the thixotropic character of said protective coating composition prior to its curing.
Dependencies are inferred from the claim text.