US 4,508,579 AGranted

Lateral device structures using self-aligned fabrication techniques

AssigneeInternational Business Machines Corporation

InventorsGeorge R. Goth, Shashi D. Malaviya

Life of this patent

Estimating the term…

Loading patent…

Abstract

Submicron lateral device structures, such as bipolar transistors, Schottky Barrier diodes and resistors, are made using self-aligned fabrication techniques and conventional photolithography. The devices are made using individual submicron silicon protrusions which extend outwardly from and are integral with a silicon pedestal therefor. Both PNP and NPN transistors may be made by diffusing appropriate dopant material into opposing vertical walls of a protrusion so as to form the emitter and collector regions. The protrusions themselves are formed by anisotropically etching the silicon using submicron insulating studs as a mask. The studs are formed using sidewall technology where a vertical sidewall section of a layer of insulating material is residual to a reactive ion etching process employed to remove the layer of insulating material.

Claims9

Dependent claims

A process for forming a semiconductor pedestal structure of tightly controlled width, comprising the steps of:

providing a body of semiconductive material;
providing a first insulating layer on said body of semiconductive material;
providing a first polysilicon layer over a first portion of said insulating layer leaving a second portion of said insulating layer exposed, said first polysilicon having a substantially vertical surface extending between said first and second portions;
providing a second insulating layer conformally over said first polysilicon layer including said vertical surface thereof and said exposed second portion of the first insulating layer, said second insulating layer over said vertical surface serving as a sidewall;
providing a second polysilicon layer conformally over said second insulating layer;
anisotropically etching said conformal second polysilicon layer forming a stud of said second polysilicon abutting said sidewall with the width of said polysilicon stud defined by the thickness of said conformal second polysilicon layer;
thermally oxidizing said polysilicon stud to convert said polysilicon stud into an essentially silicon dioxide stud;
removing said first polysilicon layer and the second insulating layer provided thereover to leave said oxide stud self-supporting and flanked on one side by said second insulating layer sidewall;
and
forming a protrusion of said semiconductive material on a pedestal thereof with the width of said protrusion defined by the width of said self-supporting stud by anisotropically etching said body of the semiconductive material surrounding said self-supporting stud using said self-supporting stud as a mask
whereby a semiconductor pedestal structure of tightly controlled width is formed.

8 more elements

A process for forming a semiconductor pedestal structure of tightly controlled submicron width, comprising the steps of:

providing a layer of silicon semiconductive material;
forming a first insulating layer on said silicon semiconductive material;
forming a first polysilicon layer over a first portion of said first insulating layer leaving a second portion of said first insulating layer exposed, said first polysilicon having a substantially horizontal surface and a vertical wall surface extending between said first and second portions;
forming a second insulating layer over said horizontal and vertical wall surfaces of said first polysilicon and over the exposed second portion of said first insulating layer;
forming a conformal second polysilicon layer of a predetermined thickness over said second insulating layer;
anisotropically etching said conformal second polysilicon layer leaving a stud of said second polysilicon abutting said wall surface said stud having a submicron width defined by the thickness of said second polysilicon layer;
thermally oxidizing said submicron polysilicon stud to convert said polysilicon stud into silicon dioxide stud;
removing said first polysilicon layer to leave a submicron self-supporting oxide stud flanked on one side by said vertical wall surface;
and
anistropically etching said semiconductor material surrounding said self-supporting stud using said self-supporting stud as a mask
whereby is formed a silicon semiconductor pedestal outwardly extending from and integral with said semiconductive material said pedestal having a submicron width defined by the width of said self-supporting oxide stud.

8 more elements

Dependencies are inferred from the claim text.