Abstract
A calcium sulfate anhydrite material is prepared from a spent absorbent resulting from desulfurization of flue gases. First the sulfite in the spent absorbent is oxidized into sulfate, preferably by heating in an oxygen containing gas, and thereafter the chloride content of the spent absorbent is reduced by heating the spent absorbent at a temperature of 600.degree.-950.degree., preferably 750.degree.-950.degree. C. together with fly ash. Said fly ash may be recovered together with the spent absorbent in the desulfurization process, or it may have been recovered separately and mixed with the spent absorbent. The product may be used as cement additive or for other purposes in which calcium sulfate anhydrite is conventionally utilized.
Claims17
A process for preparing a calcium sulfate anhydrite material of low chloride content from a chloride containing spent absorbent resulting from flue gas desulfurization by means of a basic calcium compound containing absorbent, said spent absorbent containing an amount of chloride equivalent to at least about 0.5 weight percent calcium chloride comprising the steps of
- (a) oxidizing calcium sulfite in said spent absorbent into calcium sulfate,
- (b) ensuring the presence of sufficient fly ash in intimate admixture with the spent absorbent for substantially reducing the chloride content of the spent absorbent, said fly ash resulting from the combustion of solid fuel,
- (c) heating the fly ash containing oxidized spent absorbent at a temperature of 600.degree.-950.degree. C.,
- (d) contacting the fly ash containing oxidized spent absorbent with water vapor during said heating, and
- (e) removing HCl-gas driven off by said heating.
A process for preparing a calcium sulfate anhydrite material of low chloride content from a chloride containing spent absorbent resulting from desulfurization of fly ash containing flue gas by means of a basic calcium compound containing absorbent, said spent absorbent containing an amount of chloride equivalent to at least about 0.5 weight percent calcium chloride, comprising the steps of
- (a) recovering a mixture of said spent absorbent and sufficient fly ash for substantially reducing the chloride content of the spent absorbent from the desulfurized flue gas;
- (b) oxidizing calcium sulfite in said mixture into calcium sulfate;
- (c) driving off HCl-gas by heating the mixture at 600.degree.-950.degree. C. in the access of water vapor;
- and
- (d) removing the HCl-gas driven off by said heating.
A process for preparing a calcium sulfate anhydrite material of low chloride content from a chloride containing spent absorbent resulting from flue gas desulfurization by means of a basic calcium compound containing absorbent, said spent absorbent containing an amount of chloride equivalent to at least about 0.5 weight percent calcium chloride, comprising the steps of
- (a) mixing said spent absorbent with sufficient fly ash for substantially reducing the chloride content of the spent absorbent, said fly ash resulting from the combustion of solid fuel;
- (b) oxidizing calcium sulfite in the mixture prepared in step (a) into calcium sulfate;
- (c) driving off HCl-gas by heating the mixture at 600.degree.-950.degree. C. in the access of water vapor;
- and
- (d) removing the HCl-gas driven off by said heating.
A process for preparing a calcium sulfate anhydrite material of low chloride content from a chloride containing spent absorbent resulting from flue gas desulfurization by means of a basic calcium compound containing absorbent, said spent absorbent containing an amount of chloride equivalent to at least about 0.5 weight percent calcium chloride comprising the steps of
- (a) oxidizing calcium sulfite in said spent absorbent into calcium sulfate;
- (b) preparing a mixture of the spent absorbent in which the sulfite has been oxidizing, with sufficient fly ash for substantially reducing the chloride content of the spent absorbent, said fly ash resulting from the combustion of solid fuel;
- (c) driving off HCl-gas by heating the mixture at 600.degree.-950.degree. in the access of water vapor;
- and
- (d) removing the HCl-gas driven off by said heating.