Semi-conductive compositions, based on ethylene-vinyl acetate copolymers, having adhesion to and strippability from crosslinked polyolefin substrates

A semi-conductive composition comprising an ethylene-vinyl acetate copolymer containing 15 to 30 percent by weight vinyl acetate and having a melt index of 1 to 50 g/10 min. or a chlorinated product thereof containing 3 to 40 percent by weight chlorine, carbon black, a silicone compound selected from the group consisting of silicone oils, silicone rubbers and silicone block copolymers which are liquid at normal tempertures, in an amount of about 0.3 to about 5 parts by weight and an interface crosslink inhibitor, in an amount of about 0.01 to about 1.5 parts by weight, selected from the group consisting of 2,2'-methylene-bis-(4-methyl-6-t-butyl phenol), 2,6-di-t-butyl-4-methyl phenol, 4,4'-thio-bis(6-t-butyl-2-methyl phenol), t-butyl catechol, hydroquinone, 2,5-di-t-butyl hydroquinone, 2-mercapto benzothiazole, 2,2'-thio-bis-benzothiazole, N-cyclohexyl-benzothiazole-sulfeneamide and tetramethyl thiuram disulfide.