Composition and method for tinting plastic
AssigneeTechsight Corporation
InventorHermann Weber
Life of this patent
Estimating the term…
Abstract
A solution for coating plastic material for tinting and the method of making said solution is described. The process for coating plastic material and for tinting the material is also described. This solution and process provides scratch resistance to the surface of the coated polycarbonate and CR-39 lenses, absorbs dye and permits the plastics to absorb the dye and adheres strongly to the plastic surface.
Claims11
A solution for coating plastic material for tinting comprising by volume, all percentages based upon the final concentrations:
- (a) a first mixture of:
- (1) 14.5% to 18.5% water reasonably free of dissolved solids whereby there is minimal precipitation of said solids upon addition of the other components, and
- (2) 31.5% to 51.5% of a component selected from the group consisting of n-butanol, 2-butoxyethanol, and a mixture in the range of 3:1 to 1:3 by volume of:
- (i) an alcohol selected from the group consisting of n-butanol and 2-butoxyethanol, and
- (ii) a silane compound selected from the group consisting of glycidoxypropyltrimethoxysilane and vinyltrimethylsilane
- (b) a second mixture of:
- (1) 7.5% to 17.5% alkyl titanate;
- (2) 11.5% to 21.5% methanol;
- (3) 1.7% to 2.3% of strong inorganic acid;
- (c) a third mixture of:
- (1) 3% to 9% hexamethoxymethylmelamine;
- and
- (2) 3% to 9% synthetic resin comprising urea-formaldehyde and melamine formaldehyde condensates;
- and
- (d) 25 to 83 parts per million surfactant.
A solution for coating polycarbonate material for tinting comprising by volume, all percentages based upon the final concentrations:
- (a) a first mixture of:
- (1) 10% n-butanol, and
- (2) 31.5% glycidoxypropyltrimethylsilane,
- (3) 16.5% distilled deionized water,
- (b) a second mixture of:
- (1) 12.5% tetraisopropyltitanate,
- (2) 16.5% methanol, and
- (3) 2.0% sulfuric acid,
- (c) a third mixture of:
- (1) 5.5% hexamethoxymethyl melamine, and
- (2) 5.5% synthetic resin composition comprising urea formaldehyde, and melamine formaldehyde condensates, and
- (d) 82 parts per million silicone glycol.
The method of making a solution for coating plastic material for tinting comprising the steps of:
- (1) mixing in a ratio of from 1:3 to 3:1 by volume an alcohol selected from the group n-butanol and 2-butoxyethanol and silane selected from the group consisting of glycidoxypropyltrimethoxysilane and vinyltrimethylsilane,
- (2) mixing together 31.5% to 51.5% of the mixture of the first step with 14.5% to 18.5% water;
- (3) mixing together 11.5% to 16.5% methanol, 1.7% to 2.3% of a strong acid and 7.5% to 17.5% alkyl titanate;
- (4) mixing together the mixtures of the second and third steps;
- (5) mixing together 3% to 9% hexamethoxymethylmelamine and 3% to 9% melamine formaldehyde resin solution;
- (6) mixing together the mixtures of the fourth and fifth steps;
- and
- (7) adding silicone glycol making a final concentration in the range of 25 to 83 parts per million, all percentages by volume based on the final concentration.
The method of making a solution for coating plastic material comprising the steps of:
- (1) mixing together n-butanol and glycidoxypropyltrimethoxysilane in a ratio of about 1:3,
- (2) mixing together the mixture of the first step with distilled deionized water in a a ratio of about 2.5:1,
- (3) mixing together tetraisopropyl titanate, methanol and 37% sulfuric acid in a ratio of about 6:8:1 with a stirring instrument whereby said mixture is a single phase and clear,
- (4) mixing together the mixture of the second step with the mixture of the third step in a ratio of about 2:1,
- (5) mixing together hexamethoxymethymelamine and melamine formaldehyde resin solution in a ratio of about 1:1,
- (6) mixing together the mixture of the fourth step with the mixture of resins from the fifth step in a ratio of about 8:1,
- (7) adding silicone glycol to the mixture of the prior step, said siloxane having a final concentration in the mixture of 0.082%, all ratios and percentages based on volume.