US 4,490,201 AGranted

Method of fabricating carbon composites

AssigneeThe B. F. Goodrich Company

InventorDonald H. Leeds

Life of this patent

Estimating the term…

Loading patent…

Abstract

An improved method of making a carbon composite product wherein a fabric comprised of oxidized or otherwise stabilized polyacrylonitrile fibers is heat treated and then coated with a closely controlled amount of a carbonaceous binder such as a polyimide resin. The fabric is then further heat treated to thermally fuse the resin to the fabric to form a rigid, easily handleable material. The carbonaceous binder is applied to the fabric in a manner whereby substantial encapsulation of the individual fibers is avoided. Next the material is cut into swatches of a predetermined size and shape and the segments are arranged into a basic or starting substrate having a volume greater than the desired volume of the end product. The basic substrate thus formed is then subjected to controlled temperatures and pressures to form a shaped substrate having a known fiber volume, a high degree of open porosity and a shape substantially corresponding to the shape desired of the end product. During this step, the fiber volume of the substrate is adjusted and the segments are fused together to temporarily hold them in position within the substrate. The shaped substrate thus formed is then pyrolyzed to form a carbon fibrous substrate which is densified in a freestanding configuration by the deposition of pyrolytic carbon interstitially thereof to form the desired end product. Because the portions of the fibers which are not encapsulated with binder are free to move, stresses generated in the substrate during pyrolyzation due to material shrinkage and the like are effectively distributed.

Claims10

Dependent claims

A method of making a carbon composite product comprising the steps of:

(a) selectively depositing a precisely determined, limited amount of a carbonaceous binder material onto a compressible fibrous material;
(b) subjecting said material and binder material to an elevated temperature of about 110.degree. C. for a time period of about 3 seconds to thermally fuse said binder material to the fibers of said material intermittently of the length of said fibers to form a coated material;
(c) cutting said coated material into swatches of a predetermined size and shape;
(d) constructing said swatches into a basic substrate having a volume greater than the volume of the final product;
(e) subjecting said basic substrate to controllable external pressures of up to 5000 psi at a predetermined elevated temperature necessary to thermally fuse said binder material to the fibers of said material to compress said basic substrate into a shaped substrate having a known volume and a shape substantially corresponding to the shape desired of the final product, whereby said fibers are bonded together at a multiplicity of spaced apart bonding sites being free to move in response to stresses imparted to said shaped substrate, said shaped substrate thus formed being rigid, easily handleable and transportable and being capable of further processing without the need for holding fixtures or other means of external support;
(f) subjecting said shaped substrate in a free standing configuration to elevated temperatures while controllably depositing pyrolytic material interstitially thereof, whereby said carbonaceous binder material is carbonized and said fibers are permanently bonded together by said pyrolytic material;
and
(g) continuing said interstitial deposition of pyrolytic material until the desired final product density is achieved.

5 more elements

A method of making a carbon composite product comprising the steps of:

(a) selecting a compressible fibrous material made up of fibers selected from the group consisting of pitch, rayon and polyacrylonitrile;
(b) cutting said selected material into swatches of a predetermined size and shape;
(c) selectively depositing a precisely determined, limited amount of a carbonaceous binder material onto the fibers of each of said swatches;
(d) subjecting said swatches and binder material to an elevated temperature of about 100.degree. C. and about 150.degree. C. for a time period of about 2 to 5 seconds to thermally fuse said binder material to the fibers of said swatches intermittently of the length of said fibers to form coated swatches;
(e) cutting said coated swatches into segments of a predetermined size and shape;
(f) constructing said swatches into a basic substrate having a volume greater than the volume of the final product;
(g) subjecting said basic substrate to controllable external pressures of up to 5000 psi at a predetermined elevated temperature necessary to thermally fuse said binder material to the fibers of said material to compress said basic substrate into a shaped substrate having a known volume and a shape substantially corresponding to the shape desired of the final product, whereby said fibers are bonded together at a multiplicity of spaced apart bonding sites, said fiber portions disposed intermediate said bonding sites being free to move in response to stresses imparted to said shaped substrate, said shaped substrate thus formed being rigid, easily handleable and transportable and being capable of further processing without the need for holding fixtures or other means of external support;
(h) subjecting said shaped substrate in a free standing configuration to elevated temperatures while controllably depositing pyrolytic material interstitially thereof, whereby said carbonaceous binder material is carbonized and said fibers are permanently bonded together by said pyrolytic material;
and
(i) continuing said interstitial deposition of pyrolytic material until the desired final product density is achieved.

7 more elements

Dependencies are inferred from the claim text.