A method for preparing a molecular sieve having a mole ratio of a first oxide selected from silicon oxide, germanium oxide, and mixtures thereof to a second oxide selected from aluminum oxide, gallium oxide, boron oxide, and mixtures thereof greater than 15 which comprises:

• (a) preparing an aqueous mixture containing a mole ratio of a source of a first oxide selected from silicon oxide, germanium oxide and mixtures thereof, to a source of a second oxide selected from aluminum oxide, gallium oxide, boron oxide, and mixtures thereof greater than 2, said mixture also containing sources of an imidazole salt characterized by the general structural formula:
• ##STR7## wherein X.sub.1 and X.sub.2 independently represent a branched or unbranched alkyl containing from 1 to 10 carbon atoms;
• a branched or unbranched alkyl containing from 1 to 10 carbon atoms substituted by one or more hydroxy, bromo, chloro or iodo;
• cycloalkyl containing from 5 to 10 carbon atoms;
• cycloalkyl containing 5 to 10 carbon atoms substituted by branched or unbranched lower alkyl-containing from 1 to 4 carbon atoms;
• phenyl;
• benzyl;
• phenyl substituted by one or more lower alkyl containing 1 to 4 carbon atoms;
• benzyl substituted by one or more lower alkyl containing 1 to 4 carbon atoms, or a moiety represented by the formula:
• ##STR8## wherein z is an integer of from 1 to about 20, X.sub.3 independently represents the same moieties as represented by X.sub.1, and X.sub.2, and Y.sub.1, Y.sub.2 and Y.sub.3 are as defined below,
• Y.sub.1, Y.sub.2, and Y.sub.3 independently represent hydrogen, halo, hydroxy, and lower alkyl, either branched or unbranched, containing from 1 to about 4 carbon atoms, or alternately Y.sub.1 and Y.sub.2 may be connected by the bridging group C.sub.4 H.sub.4 to form a benzimidazole with the imidazole ring, A.sup..crclbar. represents an anion which is not detrimental to the formation of the zeolite, and
• wherein further said aqueous mixture has a mole ratio of hydroxyl ion to the source of said first oxide within the range of from about 0.2 to about 0.6;
• (b) maintaining the aqueous mixture at a temperature of at least 100.degree. C. until the crystals of the desired molecular sieve form;
• and
• (c) recovering the crystals of the molecular sieve.