US 4,479,819 AGranted

Infrared polarizing glasses

AssigneeCorning Glass Works

InventorsNicholas F. Borelli, Frank Coppola, David L. Morse, Daniel A. Nolan, Thomas P. Seward, III

Life of this patent

Estimating the term…

Loading patent…

Abstract

The instant invention is directed to the preparation of glass articles exhibiting excellent polarization in the infrared portion of the spectrum from glasses characterized as containing silver halide particles therein selected from the group of AgCl, AgBr, AgI. The inventive method comprises four general steps: (a) a batch for a glass containing silver and at least one halide selected from the group of chloride, bromide, and iodide is melted and the melt shaped into a glass body of a desired geometry; (b) the glass body is subjected to a heat treatment at least above the strain point but not in excess of 50.degree. C. above the softening point of the glass for a period of time adequate to cause the generation of AgCl and/or AgBr and/or AgI particles therein, said particles ranging in size between 200-5000 .ANG.; (c) the glass body is elongated under stress at temperatures above the annealing point, but below that where said glass exhibits a viscosity of about 10.sup.8 poises, such that the particles are elongated to an aspect ratio of at least 5:1; and (d) the elongated glass body is exposed to a reducing environment at temperatures between 250.degree. C. and about 25.degree. above the annealing point of the glass to reduce the silver halide particles in the glass to metallic silver which is deposited in and/or upon the elongated particles.

Claims10

Dependent claims

A method for making a glass article exhibiting excellent polarizing properties in the infrared region of the radiation spectrum from glasses which will be phase separable or will be photochromic through the presence of silver halide particles therein selected from the group of AgCl, AgBr, and AgI, which method comprises the steps of:

(a) melting a batch for a glass containing silver and at least one halide selected from the group of chloride, bromide, and iodide;
(b) cooling and shaping said melt into a glass article of a desired configuration;
(c) subjecting said glass article to a temperature at least above the strain point, but not in excess of about 50.degree. C. above the softening point of the glass, for a sufficient length of time to cause the generation of silver halide particles therein selected from the group of AgCl, AgBr, and AgI, said particles ranging in size between about 200-5000.ANG.;
(d) elongating said glass article under stress at a temperature above the annealing point, but below that where said glass exhibits a viscosity of about 10.sup.8 poises, such that said silver halide particles are elongated to an aspect ratio of at least 5:1 and aligned in the direction of the stress;
and
(e) exposing said elongated glass article to a reducing atmosphere at a temperature above about 250.degree. C., but no higher than about 25.degree. C. above the annealing point of the glass, for a sufficient length of time to develop a reduced surface layer on said glass article having a thickness of at least 10 microns wherein at least a portion of said elongated silver halide particles are reduced to elemental silver particles having aspect ratios greater than 2:1 which are deposited in and/or upon said elongated particles, whereby said glass article exhibiting excellent polarizing properties in the infrared region of the radiation spectrum is formed.