Metal fiber reinforced bioglass composites
AssigneeUniversity of Florida
InventorsPaul L. R. Ducheyne, Larry L. Hench
Life of this patent
Estimating the term…
Abstract
Bioglass for medical and dental implants can be reinforced with metal fibers to improve strength and ductility. The resulting composites may be used as implants without need to be coated on a substrate. A method of producing the same comprises the steps of compacting and sintering an amount of metal fibers followed by impregnating the resulting porous fiber compact with molten bioglass.
Claims13
A metal fiber reinforced bioglass final composite which comprises a compacted, shaped, coherent skeletal mass of metal fibers wholly embedded in a matrix of bioglass, said skeletal mass providing pores throughout and said skeletal mass being sintered so that said pores are filled with the bioglass, the mass occupying a volume of the composite which is in the order of 10-80%, the balance being substantially bioglass.
The method of producing a metal fiber reinforced bioglass composite which comprises the steps of:
- (a) providing metal fibers whose diameters are in the range of about 20 .mu.m to about 200 .mu.m and whose lengths are in the range of about 4 mm to about 20 mm and are so related as to allow a quantity of such fibers to be compacted to a shaped, coherent skeletal mass occupying a volume of the composite which is in the order of 10-80% thereof,
- (b) compacting said quantity of such fibers to form such shaped, coherent skeletal mass,
- (c) heating said shaped, coherent skeletal mass to a sintering temperature in the range of about 1100.degree. C. to about 1300.degree. C. and for a time sufficient to assure subsequent penetration of bioglass into said shaped, coherent skeletal mass,
- (d) immersing the shaped, coherent skeletal mass while at a temperature in the range of about 400.degree. C. to about 800.degree. C. in a bath of molten bioglass which is at a temperature in the range of about 1250.degree. C. to about 1550.degree. C. but for a short time insufficient to allow the skeletal mass to reach said temperature of the bath but sufficient to permit the bioglass to penetrate and fill the voids of the shaped, coherent skeletal mass, and
- (e) recovering the metal fiber reinforced composite from the bath of step (d).