US 4,476,155 AGranted

High voltage insulators

AssigneeDow Corning Corporation

InventorRandolph G. Niemi

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of manufacturing an improved electrical high voltage coated insulator is described. The method involves applying and curing a one-part, room temperature curable silicone composition to the surface of an insulator, the insulator surface having a minimum designated arc resistance. The silicone composition is the product obtained by mixing in the substantial absence of moisture a specified polydimethylsiloxane fluid containing hydroxyl radicals, finely divided aluminum hydroxide filler, a silane of the formula R.sub.b Si(ON.dbd.X).sub.4-b and an optional condensation catalyst. The coating cures on exposure to atmospheric moisture to produce a surface adhered onto the insulator that resists the development of leakage currents and flashover failure upon exposure to electrical stress, moisture, contamination, and other outdoor weathering stresses.

Claims20

Dependent claims

A method of improving an electrical high voltage insulator comprising

(I) applying to a high voltage insulator whose surface has arc resistance of at least 750 minutes when measured according to ASTM D-2303 at 2.5 KV, a smooth, coherent, coating of a one package, room temperature curable silicone composition wherein the composition comprises the product obtained by mixing in the substantial absence of moisture,
(A) from 45 to 70 percent by weight of
(1) 100 parts by weight of polydimethylsiloxane fluid of the formula
Y(Me.sub.2 SiO).sub.a H
in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa.multidot.s at 23.degree. C., and Me is methyl radical and,
(2) from 5 to 30 parts by weight of silane of the formula
R.sub.b Si(ON.dbd.X).sub.4-b
in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the group consisting of R.sub.2 'C.dbd. and ##STR4## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive,
(B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, and the sum of (A) and (B) being 100 percent,
(C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture, then
(II) exposing the coating to atmospheric moisture for a time sufficient to cure the coating to produce a bonded, elastomeric coating of at least 0.25 mm thickness.

8 more elements

A composition suitable for coating the surface of a high voltage insulator comprising the product obtained by mixing in the substantial absence of moisture

(A) from 45 to 70 percent by weight of
(1) 100 parts by weight of polydimethylsiloxane fluid of the formula
Y(Me.sub.2 SiO).sub.a H
in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa.multidot.s at 23.degree. C., and Me is methyl radical, and
(2) from 5 to 30 parts by weight of silane of the formula
R.sub.b Si(ON.dbd.X).sub.4-b
in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the consisting of R.sub.2 'C.dbd. and ##STR5## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive,
(B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, the sum of (A) and (B) being 100 percent, and
(C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture.

6 more elements

Dependencies are inferred from the claim text.