# US 4,471,080 A · Process for making self-extinguishing, by means of red phosphorus, synthetic thermoplastic materials and products so obtained

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,471,080 A
- Document ID: US4471080A
- Status: Granted
- Kind: A
- Application number: 06/464,572
- Filed: 1983-02-07
- Granted: 1984-09-11
- Earliest claimed: 1982-02-09
- Assignees: Saffa S.p.A.
- Inventors: Gianfranco Rinaldi; Giuseppe Megler
- Web page: https://patentgrep.com/patent/US4471080A

## CPC

- C08J 3/226: {using a polymer as a carrier}
- C08K 3/02: Elements
- C08K 9/10: Encapsulated ingredients
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)
- C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09)

## Abstract

A process for making self-extinguishing thermoplastic materials based on synthetic polymeric substances by incorporation of red phosphorus into said materials, which comprises the following steps: forming a "concentrate" consisting of 30-70% of a "mother polymeric substance" and of 70-30% of red phosphorus powder previously encapsulated in a modified cationized melamine resin; incorporating said concentrate into a thermoplastic material to be made self-extinguishing and consisting of at least 50% of a polymeric substance similar to or consistent with the substance comprised in said concentrate, the amount of the above-mentioned concentrate being quantitatively so proportioned that the final self-extinguishing thermoplastic material contains 1-15% by weight of encapsulated red phosphorus.

## Claims

### Claim 1

A process for making self-extinguishing thermoplastic materials based on synthetic polymeric substances by incorporation of red phosphorus into said materials, which process comprises the steps of:
(a) preparing an in water diluted melamine precondensate by first reacting 21.62 to 25.27% melamine, 30.85 to 36.04% formaldehyde, 25.57 to 29.87% triethanolamine and 8.82 to 21.96% of monohydroxyl alcohol having less than 5 carbon atoms, and then cationizing and diluting with a mineral acid and water until a pH of 7-7.6 and a viscosity of 40-50 centipoise are reached;
(b) dispersing a micronized red phosphorus powder in the cationized solution of melamine precondensate obtained in step (a), then heating under stirring at about 100.degree. C. to precipitate said precondensate in the form of a partially cross-linked resin around the red phosphorus particles and finally drying and completing the resin's cross-linking at approx. 100.degree. C. in an inert atmosphere;
(c) forming, by mixing and extruding, a concentrate comprising 30 to 70% by weight of a mother polymeric substance and 70 to 30% by weight of the encapsulated red phosphorus obtained in step (b), said mother polymeric substance being a synthetic thermoplastic polymer selected from the group consisting of polyamides, polyolefins, copolymers from acrylonitrile-butadiene-styrene polystyrenes, vinylchloride homo- and co-polymers, vinylacetate copolymers, polycarbonates and linear polyesters; and
(d) incorporating said concentrate into a thermoplastic material to be made self-extinguishing, consisting of at least 50% by weight of any synthetic thermoplastic polymer defined in step (c), the amount of the abovesaid concentrate being quantitatively proportioned in such manner, that the final self-extinguishing thermoplastic material contains 1 to 15% by weight of said encapsulated red phosphorus powder.

### Claim 2 (depends on 1)

A process according to claim 1, in which said concentrate and said thermoplastic material to be made self-extinguishing comprise further at least a coadjuvant substance selected from the group consisting of reinforcing filler, inert fillers, pigments, dyestuffs, stabilizers, lubricants and other known conventional additives.

### Claim 3 (depends on 1)

A process according to claim 1, in which the incorporation of said concentrate into said thermoplastic material is accomplished by mixing them in the plastic state during any of the production steps of said final self-extinguishing thermoplastic material.

### Claim 4 (depends on 1)

Concentrates comprising 30-70% by weight of a synthetic thermoplastic polymer and 70-30% by weight of encapsulated red phosphorus powder, obtained by the process according to claim 1.

### Claim 5 (depends on 4)

Concentrates according to claim 4, which further comprise at least a coadjuvant substance selected from dyestuffs, stabilizers, lubricants and other known conventional additives

### Claim 6 (depends on 1)

Synthetic thermoplastic materials processable into shaped articles by means of hot-molding processes, made self-extinguishing by the process according to claim 1.