Loading patent…
AssigneesToyo Ink Manufacturing Co., Ltd., Toyo Seikan Kaisha, Ltd.
InventorsHiroo Suzuki, Tadashi Kuno, Yasuo Yoshimura, Kiyoshi Okugami, Hisashi Hotta, Shinya Otsuka
Estimating the term…
Disclosed is an aqueous coating resin composition to be applied to a metal substrate, particularly an inner surface of a metal can or can closure on which an undercoating layer is formed. This coating composition comprises an aqueous dispersion of a self-emulsifiable resin composition being obtained by neutralizing a partial reaction product of (A) an acrylic resin with (B) an epoxy resin, with ammonia or an amine selected from the group consisting of alkylamine, alcohol amines and morpholine in an amount sufficient to maintain the pH value of the composition between 5 and 11, said acrylic resin (A) being an alkali neutralizable acrylic resin having a number average molecular weight of from 10,000 to 100,000, which consists of 12 to 30% by weight of acrylic acid or methacrylic acid and 70 to 88% by weight of at least one member selected from the group consisting of styrene, methylstyrene, vinyltoluene and alkyl esters of acrylic acid and methacrylic acid having 1 to 8 carbon atoms in the alkyl group, said epoxy resin (B) being an aromatic epoxy resin having 1.1 to 2.0 epoxy groups on the average in one molecule and a number average molecular weight of at least 1,400, said partial reaction product having excess carboxyl groups in an amount sufficient to maintain the acid value of the self-emulsifiable resin composition between 30 and 200, and excess oxirane group in an amount such that the residual ratio of the oxirane content (R) is within 5 to 95%. This coating composition is excellent in the storage stability owing to the presence of excess carboxyl groups and provides a self-crosslinked coating excellent in the adhesion, processability, flavor retaining property and resistance to boiling water owing to the presence of excess oxirane groups.
An aqueous coating resin composition which comprises an aqueous dispersion of a self-emulsifiable and self-crosslinking resin composition having a pH of from 5 to 11 and being free of dispersing agents and surfactants, said resin being the neutralized product of a partial reaction product of (A) an alkali neutralizable acrylic resin having a number average molecular weight of 20,000 to 40,000, an acid value of from 80 to 240 and consisting essentially of 12 to 30% by weight of acrylic acid or methacrylic acid and 70 to 88% by weight of at least one of styrene, methylstyrene, vinyltoluene and alkyl esters of acrylic acid and methacrylic acid having 1 to 8 carbon atoms in the alkyl group, and (B) an epichlorohydrin/bisphenol epoxy resin which is selected from the group consisting of (a) epoxy resins having a number average molecular weight of 1,400 to 5,000 and two epoxy groups per molecule and (b) epoxy resins having a number average molecular weight of 2,000 to 10,000 and 1.1 to 2.0 epoxy groups per molecule, which is formed by heating an epoxy resin having a number average molecular weight of 1,400 to 5,000 and two epoxy groups per molecule in the presence of an epoxy-group modifying agent, at an (A)/(B) weight ratio of from 4/1 to 1/2, said partial reaction product of (A) and (B) having excess carboxyl groups in an amount sufficient to maintain the acid value of the self-emulsifiable and self-crosslinking resin composition between 30 and 200, and excess oxirane groups in an amount such that the residual ratio of the oxirane content (R) defined by the following formula:
Dependencies are inferred from the claim text.