Method for pretreatment of cellulosic materials
AssigneeHitachi, Ltd.
InventorsTadashi Ishibashi, Masahiko Ishida, Yoji Odawara
Life of this patent
Estimating the term…
Abstract
The disclosure is concerned with a pretreatment process for removing lignin from lignocellulosic material so as to enhance enzymatic or microbial decomposability of cellulose. The pretreatment process comprises wetting lignocellulosic material with an alkaline aqueous solution in a manner that interstices between the cellulosic material remain, and exposing the wetted cellulosic material to an ozone-containing gas so as to decompose lignin in the lignocellulosic material with a very small energy consumption.
Claims15
A method for biologically or enzymatically converting lignocellulosic materials, which comprises wetting a lignocellulosic material with an alkaline aqueous solution of an alkali metal or alkaline earth metal compound and then contacting the wetted lignocellulosic material with ozone in the state of gas-solid contact, wherein the water content of said wetted lignocellulosic material is 10 to 80% by weight and the content of alkali metal or alkaline earth metal compound is 0.001 to 10% by weight based on the total weight of the alkaline aqueous solution and the cellulosic material, to make loose the lignin from the lignocellulosic material without the lignin going into solution, and wherein the wetted lignocellulosic material is contacted with ozone without the lignin, loosened by the treatment with the aqueous liquid of alkali metal or alkaline earth metal compound, having previously gone into solution, to decompose the loose lignin, and subjecting the treated lignocellulosic material to biological or enzymatic decomposition treatment.
A method for biologically or enzymatically converting lignocellulosic material, which comprises impregnating a chopped lignocellulosic material with an aqueous liquid of alkali metal or alkaline earth metal compound in such a manner that interstices of the chopped lignocellulosic material remain, wherein the water content of the impregnated lignocellulosic material is 10 to 80% by weight and wherein the content of alkali metal or alkaline earth metal compound is 0.001 to 10% by weight based on the total weight of the alkali metal or alkaline earth metal compound, water and lignocellulosic material, to make loose the lignin of the lignocellulosic material without the lignin going into solution;
- contacting the impregnated lignocellulosic material with an ozone-containing gas without the lignin, loosened by said impregnating, having previously gone into solution, keeping gas-solid contact between the ozone-containing gas and the impregnated lignocellulosic material, whereby the lignin is preferentially decomposed by the ozone-containing gas;
- and subjecting the treated cellulosic material to biological or enzymatic decomposition treatment.