Infrared transmitting fiber optical waveguide extruded from halides of the metal thallium and the method of preparation
AssigneeHughes Aircraft Company
InventorsDouglas A. Pinnow, Anthony L. Gentile, Arlie G. Standlee, Arthur J. Timper
Life of this patent
Estimating the term…
Abstract
There is disclosed a fiber optic waveguide which is particularly suited for infrared radiation transmission at extended wavelengths. The core of the waveguide is fabricated from heavy ionic compounds selected from metal halides in order to achieve such extended infrared transparency. While it is impossible to prepare these materials into optical fibers using conventional fiber drawing techniques, the present invention teaches how such materials may be prepared into optical fibers using an extrusion process at elevated temperatures and high pressures.
Claims4
The method of making an optical fiber from thallium bromoiodide, comprising the steps of:
- heating a quantity of thallium bromoiodide to a temperature which is in the range of 200.degree. C. to 350.degree. C.;
- and
- extruding an optical fiber from said heated material.
The method of making an optical fiber from thallium bromoiodide, comprising the steps of:
- heating a quantity of thallium bromoiodide to a temperature which is in the range of 200.degree. C. to 350.degree. C.;
- and
- extruding an optical fiber from said heated material at a rate of several centimeters per minute.
As a new article of manufacture, an optical fiber of thallium bromoiodide which is extruded in the presence of heat in the range of 200.degree. C. to 350.degree. C.
As a new article of manufacture, an optical fiber of thallium bromoiodide which is extruded in the presence of heat in the range of 200.degree. C. to 350.degree. C. at a rate of several centimeters per minute.