US 4,443,415 AGranted

Recovery of V.sub.2 O.sub.5 and nickel values from petroleum coke

AssigneeAmax Inc.

InventorsPaul B. Queneau, Robert F. Hogsett, Leo W. Beckstead, Dale K. Huggins

Life of this patent

Estimating the term…

Loading patent…

Abstract

Vanadium and nickel values are selectively recovered from a petroleum coke residue by slurrying the coke in an aqueous solution of sodium carbonate providing an excess of the stoichiometric amount of sodium for formation of sodium vanadate and sodium sulfate, and then digesting the slurry at moderately elevated temperature in a pressurized autoclave under an oxygen overpressure supplying at least the stoichiometric amount of oxygen based on the vanadium and sulfur content of the slurry and advantageously sufficient additional oxygen to provide the thermal requirements of the digestion step by oxidation of carbon. In a continuous embodiment, the feed slurry temperature and feed solids content are adjusted according to a substantially inversely correlated relationship. The digestion temperature for a given total pressure and gas flow rate in the autoclave is adjusted to generate a pregnant liquor containing about 20 gpl to about 100 gpl of vanadate (V.sub.2 O.sub.5) from which at least about 50% of the input water has been converted to steam during the digestion. The vanadate liquor is separated from the digestion residue, which is then sequentially selectively leached for recovery therefrom of nickel and residual vanadium values.

Claims8

Dependent claims

A process for recovering vanadium and nickel values from petroleum coke comprising carbonaceous matter assaying at least about 50 wt. % carbon and also containing vanadium, at least a portion of which is in an oxidation state no higher than trivalent, iron, in an amount less than about 10% by weight of the vanadium as V.sub.2 O.sub.5, and nickel values, as well as one or more compounds of sulfur, comprising

(a) establishing a slurry of the coke in an aqueous solution of sodium carbonate in an amount to provide an excess of sodium over the stoichiometric amount for formation of NaVO.sub.3 and Na.sub.2 SO.sub.4,
(b) digesting the slurry in an autoclave at a digestion temperature of about 250.degree. C. to about 320.degree. C. under an oxygen overpressure comprising at least the stoichiometric amount of oxygen for oxidation of the vanadium in the trivalent or lower oxidation state to the pentavalent state, to form an aqueous sodium vanadate liquor containing at least about 75% of the vanadium values fed in the slurry and a digestion residue containing vanadium, iron, and nickel values as well as any unoxidized carbonaceous matter,
(c) separating the sodium vanadate liquor from the digestion residue,
(d) leaching the digestion residue with an aqueous solution of an alkali metal compound selected from the group consisting of carbonates and hydroxides to produce a vanadate leach liquor and a first leach residue,
(e) filtering the vanadate leach liquor from the first leach residue,
(f) leaching the first leach residue with an aqueous solution of a mineral acid having a pH value between about 3 and about 6 to produce a nickel leach liquor and a second leach residue, and
(g) filtering the nickel leach liquor from the second leach residue.

4 more elements

A continuous process for recovering vanadium and nickel values from a petroleum coke comprising carbonaceous matter assaying at least about 50 wt. % carbon and having a fuel value of at least about 5000 kcal/kg of coke and also containing vanadium, at least a portion of which is in an oxidation state no higher than trivalent, iron, in an amount less than about 10% by weight of the vanadium as V.sub.2 O.sub.5, and nickel values, as well as one or more compounds of sulfur, comprising

(a) establishing a slurry of the coke in an aqueous solution of sodium carbonate in an amount to provide an excess of sodium over the stoichiometric amount for formation of NaVO.sub.3 and Na.sub.2 SO.sub.4,
(b) feeding the slurry to an autogenously heated autoclave to which oxygen-bearing gas is fed and from which an off-gas stream containing water vapor and oxides of carbon is withdrawn to provide in the autoclave an oxygen overpressure of about 0.07 kg/cm to about 70 kg/cm- and a given total pressure of about 40 kg/cm.sup.2 to about 200 kg/cm.sup.2,
(c) digesting the slurry in said autoclave at a digestion temperature of about 250.degree. C. to about 320.degree. C. to oxidize at least a portion of the carbonaceous matter in the slurry to form gaseous oxides of carbon and to oxidize the vanadium in the trivalent or lower state to the pentavalent state, thereby dissolving at least about 75% of the vanadium values in the coke as a sodium vanadate liquor and forming a digestion residue containing vanadium, iron, and nickel values as well as any unoxidized carbonaceous matter,
wherein said digestion temperature is substantially inversely correlated to the gas flow rate and substantially directly correlated to the total pressure,
and wherein the digestion temperature is adjusted by adjusting the solids content of the slurry established in step (a) to about 10 to about 300 grams of solids per liter of slurry and adjusting the temperature of the slurry established in step (a) to about 5.degree. C. to about 95.degree. C., wherein said slurry temperature is substantially inversely correlated to the slurry solids content, to convert at least about 50% of the water fed in the slurry to steam and to provide that the sodium vanadate liquor contains about 20 gpl to about 100 gpl of vanadium as V.sub.2 O.sub.5,
(d) separating the sodium vanadate liquor from the digestion residue,
(e) leaching the digestion residue with an aqueous solution of an alkali metal compound selected from the group consisting of carbonates and hydroxides to produce a vanadate leach liquor and a first leach residue,
(f) filtering the vanadate leach liquor from the first leach residue,
(g) leaching the first leach residue with an aqueous solution of a mineral acid having a pH value between about 3 and about 6 to produce a nickel leach liquor and a second leach residue, and
(h) filtering the nickel leach liquor from the second leach residue.

7 more elements

Dependencies are inferred from the claim text.